Notch sensitivity of cast AZ31 magnesium alloy

0024658 - ÚFM 2006 RIV SK eng J - Journal Article
Kunz, Ludvík - Lukáš, Petr - Estrin, Y. - Zúberová, Z.
Notch sensitivity of cast AZ31 magnesium alloy.
[Vrubová citlivost lité hořčíkové slitiny AZ31.]
Materiálové inžinierstvo - Materials Engineering. Roč. 12, č. 3 (2005), s. 88-91. ISSN 1335-0803.
[Degradácia konštrukčných materiálov 2005. Terchová - Biely Potok, 05.09.2005-07.09.2005]
R&D Projects: GA MŠMT(CZ) 1P05ME804
Institutional research plan: CEZ:AV0Z20410507
Keywords : notch sensitivity * magnesium alloy * fatigue lifetime
Subject RIV: JG - Metallurgy

Cast AZ31 alloy was found to be totally insensitive to circumferential notches with stress concentration factor of 2.49. An attempt has been made to explain this behaviour on the basis of fractographic determination of the critical crack size and using notch theory based on fracture mechanics. The S-N curve of cast Mg AZ31 alloy exhibits a pronounced knee in the region of 10 to 5 cycles. The endurance limit based on 10 to 7 cycles is 40 MPa.

Bylo zjištěno, že litá hořčíková slitina AZ31 je při únavovém namáhání zcela necitlivá na přítomnost obvodového vrubu s teoretickým součinitelem koncentrace napětí 2,49. Byl učiněn pokus vysvětlit toto chování na základě fraktograficky zjištěné velikosti kritické trhliny s použitím vrubové teorie založené na lomově-mechanických představách. S-N křivka slitiny AZ31 vykazuje výrazné koleno v oblasti 10 na 5 cyklů. Smluvní mez únavy na bázi 10 na 7 cyklů je 40 MPa.
Permanent Link: http://hdl.handle.net/11104/0115163