Number of the records: 1  

Wear characteristics and defects analysis of friction stir welded joint of aluminium alloy 6061-t6

  1. 1.
    0455231 - ÚGN 2016 RIV PL eng J - Journal Article
    Kumar, R. - Chattopadhyaya, S. - Hloch, Sergej - Krolczyk, G. - Legutko, S.
    Wear characteristics and defects analysis of friction stir welded joint of aluminium alloy 6061-t6.
    Eksploatacja i Niezawodnosc-Maintenance and Reliability. Roč. 18, č. 1 (2016), s. 128-135. ISSN 1507-2711. E-ISSN 1507-2711
    Institutional support: RVO:68145535
    Keywords : Friction stir welding (FSW) * grinding machine * Field Emission Scanning Electron Microscope (FESEM)
    Subject RIV: JQ - Machines ; Tools
    Impact factor: 1.145, year: 2016
    http://www.ein.org.pl/2016-01-17

    This paper deals with the wear characteristics and defects developed during friction stir welding at different process parameter of aluminium alloy (AA) 6061-T6 having thickness 6 mm. Four welded samples are prepared with rotational speed 500 rpm, 710 rpm, 1000 rpm and with welding speed of 25 mm/min & 40 mm/min. Welded samples and base material are put in wear condition under grinding machine for 120 s. Material removal is measure by taking the difference of weight before and after wear. Different types of defects and fracture are observed on the wear surface. These defects and fractures are analysed under field emission scanning electron microscope (FESEM). It is concluded that material removal from welded sample is less compared to base metal, hence wear resistance increases after friction stir welding.
    Permanent Link: http://hdl.handle.net/11104/0255880

     
    FileDownloadSizeCommentaryVersionAccess
    UGN_0455231.pdf11.9 MBPublisher’s postprintopen-access
     
Number of the records: 1  

  This site uses cookies to make them easier to browse. Learn more about how we use cookies.