Influence of SiON interlayer on the diamond/GaN heterostructures studied by Raman and SIMS measurements
- 1.0546598 - FZÚ 2022 RIV CH eng J - Journal Article
Izsák, Tibor - Vanko, G. - Babčenko, Oleg - Vincze, A. - Vojs, M. - Zaťko, B. - Kromka, Alexander
Influence of SiON interlayer on the diamond/GaN heterostructures studied by Raman and SIMS measurements.
Materials Science and Engineering B-Advanced Functional Solid-State Materials. Roč. 273, Nov. (2021), č. článku 115434. ISSN 0921-5107. E-ISSN 1873-4944
R&D Projects: GA MŠMT LM2018110; GA MŠMT(CZ) 8X20035; GA MŠMT(CZ) EF16_019/0000760
Grant - others:OP VVV - SOLID21(XE) CZ.02.1.01/0.0/0.0/16_019/0000760
Institutional support: RVO:68378271
Keywords : polycrystalline diamond * GaN * Raman spectroscopy * stress * SIMS
OECD category: Coating and films
Impact factor: 3.407, year: 2021
Method of publishing: Limited access
https://doi.org/10.1016/j.mseb.2021.115434
The effect of silicon oxynitride (SiON) layer on the thermally-induced stress of diamond-coated AlGaN/GaN heterostructures was studied by Raman and SIMS spectroscopy. Diamond films (0.8 or 2.8 µm in thickness) were grown by MWCVD on selected areas of AlGaN/GaN/Si substrates with SiON interlayer. The stress in diamond became tensile for the thinner strip in the range of 0÷0.5 GPa and compressive for the thicker strip in the range of -0.6 ÷ -0.1 GPa both measured at temperatures ranging from 50 to 400°C. The applied SiON interlayer positively influenced the induced stress (Δstress decreased by about 0.14 GPa compared to the sample without SiON) independently on the thickness of the diamond film. SIMS depth profiling was applied to analyse the influence of diamond CVD on the AlGaN/GaN interface of SiON passivated samples. As observed, the hydrogen and carbon atoms were trapped in the SiON which acted as a stop layer.