Investigation of MOVPE-grown zincblende GaN nucleation layers on 3C-SiC/Si substrates

0509851 - ÚFM 2020 RIV NL eng J - Journal Article
Lee, L.Y. - Frentrup, M. - Vacek, Petr - Massabuau, Fabien C. P. - Kappers, Menno J. - Wallis, David J. - Oliver, Rachel A.
Investigation of MOVPE-grown zincblende GaN nucleation layers on 3C-SiC/Si substrates.
Journal of Crystal Growth. Roč. 524, OCT (2019), č. článku 125167. ISSN 0022-0248. E-ISSN 1873-5002
R&D Projects: GA MŠMT(CZ) EF16_027/0008056
Institutional support: RVO:68081723
Keywords : Atomic force microscopy * Nucleation * X-ray diffraction * Metalorganic vapor phase epitaxy * Nitrides * Semiconducting gallium compounds
OECD category: Electrical and electronic engineering
Impact factor: 1.632, year: 2019
Method of publishing: Limited access
https://www.sciencedirect.com/science/article/pii/S0022024819303823?via%3Dihub

Cubic zincblende (zb-)GaN nucleation layers (NLs) grown by MOVPE on 3C-SiC/Si substrates were studied to determine their optimal thickness for subsequent zb-GaN epilayer growth. The layers were characterised by atomic force microscopy, X-ray diffraction and scanning transmission electron microscopy. The as-grown NLs, with nominal thicknesses varying from 3nm to 44nm, consist of small grains which are elongated in the [1−10] direction, and cover the underlying SiC surface almost entirely. Thermal annealing of the NLs by heating in a H2/NH3 atmosphere to the elevated epilayer growth temperature reduces the substrate coverage of the films that are less than 22nm thick, due to both material desorption and the ripening of islands. The compressive biaxial in-plane strain of the NLs reduces with increasing NL thickness to the value of relaxed GaN for a thickness of 44nm. Both the as-grown and annealed NLs are crystalline and have high zincblende phase purity, but contain defects including misfit dislocations and stacking faults. The zb-GaN epilayers grown on the thinnest NLs show an enhanced fraction of the wurtzite phase, most likely formed by nucleation on the exposed substrate surface at elevated temperature, thus dictating the minimum NL thickness for phase-pure zb-GaN epilayer growth.