High Temperature Low Cycle Fatigue Characteristics of Grit Blasted Polycrystalline Ni-base Superalloy

  1. 1.
    0447855 - ÚFM 2017 RIV CH eng C - Conference Paper (international conference)
    Šulák, Ivo - Obrtlík, Karel - Čelko, L.
    High Temperature Low Cycle Fatigue Characteristics of Grit Blasted Polycrystalline Ni-base Superalloy.
    Advances in Fracture and Damage Mechanics XIV. Zurich: Trans Tech Publications, 2016 - (Bajić, D.; Tonković, Z.; Aliabadi, F.), s. 73-76. Key Engineering Materials, 665. ISBN 978-3-03835-541-0. ISSN 1013-9826.
    [FDM 2015 - International Conference on Fracture and Damage Mechanics /14./. Budva (ME), 21.09.2015-23.09.2015]
    R&D Projects: GA ČR(CZ) GA15-20991S; GA TA ČR(CZ) TA04011525
    Institutional support: RVO:68081723
    Keywords : Grit Blasting * Fatigue life * Cyclic stress-strain response * High temperature fatigue * IN 713LC
    Subject RIV: JL - Materials Fatigue, Friction Mechanics

    The present work is focused on the study of low cycle fatigue behavior of grit blasted nickel-base superalloy Inconel 713LC (IN 713LC). Grit blasting parameters are obtained. Button end specimens of IN 713LC in as-received condition and with grit blasted surface were fatigued under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of both materials were obtained. Both materials exhibit the same stress-strain response. It has not been observed any improvement or reduction of low cycle fatigue life in representation of total strain amplitude versus number of cycles to failure of grit blasted material in comparison with as-received material. Surface relief and fracture surface were observed in SEM. The little effect of surface treatment on fatigue characteristics is discussed.