Reactivity of the tin homolog of POSS, butylstannoxane dodecamer, in oxygen-induced crosslinking reactions with an organic polymer matrix: study of long-time behavior

0444156 - ÚMCH 2016 RIV NL eng J - Journal Article
Rodzen, Krzysztof - Strachota, Adam - Ribot, F. - Matějka, Libor - Kovářová, Jana - Trchová, Miroslava - Šlouf, Miroslav
Reactivity of the tin homolog of POSS, butylstannoxane dodecamer, in oxygen-induced crosslinking reactions with an organic polymer matrix: study of long-time behavior.
Polymer Degradation and Stability. Roč. 118, August (2015), s. 147-166. ISSN 0141-3910. E-ISSN 1873-2321
R&D Projects: GA ČR GAP108/11/2151
Institutional support: RVO:61389013
Keywords : POSS * stannoxane * reactivity
Subject RIV: CD - Macromolecular Chemistry
Impact factor: 3.120, year: 2015

The chemical activity of the heavier POSS homolog, n-butylstannoxane dodecamer cage, in an epoxy matrix containing polopropylene oxide (PPO) chains was studied in detail, especially the long-time development of the effect and its limits in time at different concentrations. A multi-method investigation was carried out, employing spectrometric analysis of chemical composition (NMR, IR), TEM, thermogravimetry, weight loss analysis during isothermal oxidation at 180 °C, as well as dynamic-mechanical thermal analysis (DMTA) of intact and of oxidized epoxy/stannoxane hybrids. The PPO segments of the matrix were found to be preferentially degraded by oxidation or by anaerobic pyrolysis, while at the same time these segments are the sites of crosslinking reactions with stannoxane, which counteract matrix degradation. It was demonstrated, that the cages undergo repeated reactions on the Sn atoms, and remain finely dispersed and well-accessible even after long oxidation times. The repeated reactions also explain the observed very strong stabilizing effect of stannoxane at very low concentrations. Efficient stabilization against the degradation of the mechanical properties was found to require higher – but still very low – concentrations, than the stabilization against weight loss. Interestingly, certain amounts of stannoxane caused simultaneously enhanced weight losses and a mechanical reinforcement due to a higher amount of radical reactions.