Experimental investigation of high power picosecond 1.06μm pulse propagation in Bragg fibers

0396857 - ÚFE 2014 RIV US eng C - Conference Paper (international conference)
Jelínek, M. - Kubeček, V. - Jelínková, H. - Matějec, Vlastimil - Kašík, Ivan - Podrazký, Ondřej
Experimental investigation of high power picosecond 1.06μm pulse propagation in Bragg fibers.
Nonlinear Optics and Applications VII (Proceedings of SPIE 8772). Vol. 8772. BELLINGHAM: SPIE, 2013 - (Bertolotti, M.; Haus, J.; Zheltikov, A.). ISBN 978-0-8194-9574-7. ISSN 0277-786X.
[Nonlinear Optics and Applications VII. Prague (CZ), 15.04.2013-17.04.2013]
R&D Projects: GA ČR GAP102/12/2361
Institutional support: RVO:67985882
Keywords : Silica Bragg fiber * MCVD method * laser power delivery
Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering

In this paper we present fabrication and characterization of the laboratory-designed Bragg fiber. The fiber consisted of a silica core with the diameter of 26 μm surrounded by 3 pairs of circular Bragg layers with a refractive index contrast up to 0.033. Spectral attenuation was measured using a halogen lamp source and the cut-back method resulting in the attenuation coefficient of 0.175 dB/m at 1064 nm. Experiments on high power laser radiation delivery were performed using a laboratory-designed passively mode-locked Nd:YAG laser system generating pulses with the duration of 20 ps and energy of 15 μJ at the wavelength of 1064 nm. The attenuation coefficient measurements resulted in a value of 0.168 ± 0.005 dB/m. The delivered beam spatial profile was detected in the far-field zone in the distance of ~1 cm from the fiber output face. The beam had a circular symmetry with almost Gaussian intensity profile. Bending losses were measured on 1-m long fiber segments using mandrels with different diameters. The bending losses were equal to zero at mandrel diameters greater than 50 mm. Decreasing the mandrel diameter, the bending losses were slightly increasing to a value of 3.6 dB/turn at the mandrel diameter of 8 mm. Stimulated Raman scattering in the fiber was also investigated. The Raman threshold intensity in the fiber core for a 1-m long fiber segment was 113 GWcm2. In a 48-m long fiber, generation up to the 3rd Stokes component was observed together with the spectral broadening up to 1650 nm
Permanent Link: http://hdl.handle.net/11104/0232219