High-cycle fatigue of Ni-base superalloy Inconel 713LC.
International Journal of Fatigue. Roč. 32, č. 6 (2010), s. 908-913. ISSN 0142-1123. E-ISSN 1879-3452
Grant CEP: GA MPO FT-TA4/023; GA MŠMT MEB080812
Výzkumný záměr: CEZ:AV0Z20410507
Klíčová slova: IN 713LC * High-cycle fatigue * Effect of mean stress * Fractography * Casting defetcts * Extreme value statistics
Kód oboru RIV: JL - Únava materiálu a lomová mechanika
Impakt faktor: 1.799, rok: 2010 ; AIS: 0.68, rok: 2010
DOI: https://doi.org/10.1016/j.ijfatigue.2009.02.042

Fatigue strength of three nominally identical batches of cast Ni-base superalloy INCONEL 713LC under load symmetrical cycling and cycling with tensile mean load was experimentally determined in high-cycle fatigue region at a temperature of 800 °C in air. Examination of fracture surfaces, crack initiation sites, microstructure and casting defects has been performed. Statistical method of largest extreme value distribution has been applied to characterize the casting defect distribution. The aim of the study was to evaluate the mean stress effect on high-cycle fatigue life, to explain the scatter of fatigue life data and a scatter related to material produced under nominally identical production conditions.