SrTiO.sub.3./sub.:Cr nanocrystalline powders: size effects and optical properties

0328504 - FZÚ 2010 RIV GB eng J - Journal Article
Trepakov, Vladimír - Potůček, Zdeněk - Makarova, Marina - Dejneka, Alexandr - Sazama, Petr - Jastrabík, Lubomír - Bryknar, Z.
SrTiO₃:Cr nanocrystalline powders: size effects and optical properties.
[Nanokrystalické prášky SrTiO₃:Cr : rozměrový efekt a optické vlastnosti.]
Journal of Physics-Condensed Matter. Roč. 21, č. 37 (2009), 375303/1-375303/5. ISSN 0953-8984. E-ISSN 1361-648X
R&D Projects: GA ČR GA202/08/1009; GA AV ČR KJB100100703; GA AV ČR KAN301370701; GA MŠMT(CZ) 1M06002
Institutional research plan: CEZ:AV0Z10100522; CEZ:AV0Z40400503
Keywords : SrTiO₃:Cr nanocrystalline powders * size effects * optical properties
Subject RIV: BM - Solid Matter Physics ; Magnetism
Impact factor: 1.964, year: 2009

The crystal structure, optical absorption, and photoluminescence of chromium impurity centers were studied in nanocrystalline SrTiO3:Cr (0.1 mol%) powders with average particle size within the range 13–100 nm prepared by the Pechini-type polymeric sol–gel method.The optical absorption edge and the zero-phonon R-line (2E → 4A2) of luminescence of the octahedral Cr3+ centers shifted to higher energies with decreasing nanoparticle size.

Byla studována krystalová struktura,optická absorpce a fotoluminiscence příměsových center chrómu v nanokrystalických prášcích SrTiO3:Cr (0.1 mol%) s průměrnou velikostí částic v rozsahu 13 - 100 nm připravovaných pomocí Pechiniho sol-gel metody z polymerního prekurzoru.Optická absorpční hrana a poloha bezfononové emisní R-linie (2E → 4A2) odpovídající oktaedrickým Cr3+ centrům se posouvají k vyšším energiím s poklesem velikosti nanočástic.