Low cycle fatigue of ductile cast iron with 2,8 % nickel
- 1.0324506 - ÚFM 2009 RIV CZ eng K - Conference Paper (Czech conference)
Tesařová, H. - Petrenec, Martin - Pacal, B. - Musilová, I.
Low cycle fatigue of ductile cast iron with 2,8 % nickel.
[Nízkocyklová únava tvárné litiny s 2,8 % niklu.]
45. SLÉVÁRENSKÉ DNY a 5. mezinárodní PhD konference. Vol. 5. Brno: VUT Brno, 2008, s. 39-45. ISBN 978-80-214-3646-6.
[45. slévárenské dny a 5. mezinárodní PhD konference. Brno (CZ), 13.05.2008-15.05.2008]
R&D Projects: GA AV ČR 1QS200410502; GA ČR GD106/05/H008
Institutional research plan: CEZ:AV0Z20410507
Keywords : Low cycle fatigue * ferritic ductile cast iron * Fatigue crack initiation
Subject RIV: JL - Materials Fatigue, Friction Mechanics
Cast ductile iron with the ferritic matrix alloying with 2.8% Ni was subjected to cycling with constant strain amplitudes and the cyclic stress-strain response and fatigue life were studied experimentally. The original microstructure is documented using light microscope. Fracture surface was studied using scanning electron microscopy. Manson-Coffin and Basquin laws can reasonably approximate the fatigue life data. Fatigue crack initiation from shrinkage cavity is documented.
Tvárna litina s feritickou matricí legována 2,8% Ni byla cyklicky zatěžována konstantními amplitudami celkové deformace za účelem experimentálního studia cyklické napěťově-deformační odezvy a únavové životnosti.Původní mikrostruktura je dokumentována světelným mikroskopem. Lomové plochy byly pozorovány skenovacím elektronovým mikroskopem pro studium míst iniciace únavových trhlin jež byla slévárenské defekty a grafitidké částice./navovou životnost lzevelmi dobře aproximovat pomocí Manson-Coffin a Basquin závislostí.