Mechanical behavior of polysiloxane matrix - based composite reinforced with basalt fibres at elevated temperatures

0318697 - ÚSMH 2009 RIV CZ eng J - Journal Article
Černý, Martin - Sucharda, Zbyněk - Glogar, Petr
Mechanical behavior of polysiloxane matrix - based composite reinforced with basalt fibres at elevated temperatures.
[Kompozitní materiály vyztužené čedičovými vlákny s pyrolyzovanou polysiloxanovou matricí.]
Acta geodynamica et geomaterialia. Roč. 5, č. 4 (2008), s. 399-406. ISSN 1214-9705. E-ISSN 2336-4351
R&D Projects: GA ČR GA106/05/0817
Institutional research plan: CEZ:AV0Z30460519
Keywords : basalt fibre * composite * mechanical behaviour
Subject RIV: JI - Composite Materials

Unidirectionally reinforced basalt fibre composites with a matrix derived by partial pyrolysis at 650 – 750 °C from commercially available polysiloxane precursors were studied. The composite pyrolysed at 650 °C revealed the best room – temperature mechanical properties. Its exploitation in a common environment up to 550 °C is possible but some reduction of strength and fracture toughness must be taken in consideration which takes place already after its short-time exposition in hot air.

Byly studovány kompozity jednosměrně vyztužené čedičovými vlákny s matricí připravenou částečnou pyrolýzou (při 650 – 750°C) z komerčně dostupných polysiloxanových prekurzorů. Kompozity pyrolyzované při 650°C mají nejlepší mechanické vlastnosti při pokojové teplotě. Jejich použití v běžném prostředí je možné až do 550°C, ale je třeba počítat s jistým poklesem pevnosti a lomové houževnatosti, k nimž dochází již při krátkodobé expozici v horkém vzduchu.
Permanent Link: http://hdl.handle.net/11104/0168038