Problems of crystallization of B2-FeAl based alloys

0313874 - FZÚ 2009 RIV CZ eng C - Conference Paper (international conference)
Kopeček, Jaromír - Jurek, Karel - Šíma, Vladimír - Lejček, Pavel
Problems of crystallization of B2-FeAl based alloys.
[Problémy krystalizace slitin na bázi B2-FeAl.]
Proceedings of 17th European Conference on Fracture. Brno: VUTIUM Brno, 2008 - (Pokluda, J.; Lukáš, P.; Šandera, P.; Dlouhý, I.), s. 2495-2501. ISBN 978-80-214-3692-3.
[17th European Conference on Fracture. Brno (CZ), 02.09.2008-05.09.2008]
R&D Projects: GA ČR GA106/06/0019
Institutional research plan: CEZ:AV0Z10100520
Keywords : Fe-40Al * iron aluminides * carbides * crystal growth
Subject RIV: BM - Solid Matter Physics ; Magnetism

Although the main source of the grain boundary weakness in FeAl arises from environmental embrittlement, important source seems to be of the intrinsic nature. The single crystals prepared by Bridgman method contain the star cracks when grown with growth rates higher than 9 mm/h. At lower growth rates the stress induced by solidification is not high enough to cause crack initiation.

Ačkoli je hlavním zdrojem křehkosti hranic zrn v FeAl prostředí, dalším důležitým zdrojem je i vnitřní povaha slitiny. Monokrystaly připravené Bridgmanovou metodou rychlostí vyšší než 9 mm/h obsahují hvězdicovité praskliny, zatímco při nižších rychlostech nejsou napětí indukovaná tuhnutím dostatečně vysoká, aby způsobily iniciaci trhliny.