Fractal Anisotropy and Heterogeneity of Fracture Surfaces in Steel

0313025 - ÚFM 2009 RIV CZ eng K - Conference Paper (Czech conference)
Strnadel, B. - Dlouhý, Ivo
Fractal Anisotropy and Heterogeneity of Fracture Surfaces in Steel.
[Fraktální anisotropie a heterogenita lomových ploch oceli.]
New Methods of Damage and Failure Analysis of Structural Parts. Ostrava: VŠB - TU Ostrava, 2008, s. 365-372. ISBN 978-80-248-1813-9.
[New Methods of Damage and Failure Analysis of Structural Parts. Ostrava (CZ), 08.09.2008-12.09.2008]
R&D Projects: GA ČR(CZ) GA106/06/0646
Institutional research plan: CEZ:AV0Z20410507
Keywords : brittle crack * fracture micromechanism * transgranular fracture * intergranular fracture * fractal dimension
Subject RIV: JL - Materials Fatigue, Friction Mechanics

The change in the fractal dimension of the fracture surface demonstrates a wavy character and dispersion depending on the microstructural state of the tested steel. The results of the fractal analysis in the crack growth direction and across the entire crack front were used as the basis for a reconstruction of the geometry of the fracture surface. The competing effects of transgranular and intergranular brittle fracture may lead to increased roughness of the fracture surface and its fractal dimension.

Závislosti fraktální dimenze lomové plochy vykazují vlnový charakter a rozptyl v závislosti na mikrosturkturním stavu testované oceli. Výsledky fraktální analýzy ve směru šíření trhliny a podél čela trhliny byly použity pro rekonstrukci geometrie lomové plochy. Důsledky konkurence transkrystalického a interkrystalického křehkého lomu mohou vést k zvýšené drsnosti lomové plochy a její fraktální dimenze.