0108357 - UFM-A 20043178 RIV DE eng J - Journal Article
David, Bohumil - Pizúrová, Naděžda - Schneeweiss, Oldřich - Bezdička, Petr - Alexandrescu, R. - Morjan, I. - Crunteanu, A. - Voicu, I.
Iron/graphite core-shell structured nanoparticles prepared by annealing of Fe-C-N composite.
[Nanočástice železa pokryté grafitem připravené žíháním Fe-C-N nanokompozitu.]
Physica Status Solidi C. Roč. 12, č. 12 (2004), s. 3418-3422. ISSN 1610-1634.
[Second Seeheim Conference on Magnetism. Seeheim, 27.06.2004-01.07.2004]
R&D Projects: GA ČR GA202/01/0668; GA AV ČR KSK1010104
Institutional research plan: CEZ:AV0Z2041904
Keywords : nanoparticles * iron/graphite * core-shell
Subject RIV: BM - Solid Matter Physics ; Magnetism

We are reporting the core-shell structured iron/graphite nanoparticles formed during annealing of the nanopowder prepared by laser pyrolysis of gas phase reactants. The originally synthesized Fe-C-N based nanocomposite powder has been characterized by TEM, XRD and magnetic measurements. Nanopowder was heated up to 800C at ~ 1 Pa vacuum. Presence of iron nanoparticles with the mean diameter of 40 nm in the annealed state of nanopowder was proved by XRD and TEM. Mössbauer spectroscopy was used for characterization of the synthesized/annealed nanopowder.

V článku se zabýváme nanočásticemi se strukturou jádro-slupka. Jádro částic je tvořené železem a slupka je z grafitu. Tyto nanočástice vznikly žíháním nanoprášku vyrobeného laserovou pyrolýzou plynných reaktantů. Nanoprášek, který byl syntetizován z plynných prekurzorů obsahujících prvky Fe, C, N, byl studován pomocí TEM, XRD a magnetických měření. Nanoprášek byl následně vyžíhán při 800°C ve vakuu. Přítomnost železných nanočástic se středním průměrem 40 nm ve vyžíhaném nanoprášku byla dokázána XRD a TEM analýzou. Pro určení fázového složení syntetizovaného a vyžíhaného nanoprášku byla použita Mössbauerova spektroskopie.