0100237 - FZU-D 20040217 RIV GB eng J - Journal Article
Potůček, Zdeněk - Bryknar, Z. - Schulz, H. J.
Thermoluminescence of nominally pure KTaO₃ crystals.
[Termoluminiscence nominálně čistých krystalů KTaO₃.]
Radiation Effects and Defects in Solids. Roč. 157, - (2002), s. 1021-1024. ISSN 1042-0150. E-ISSN 1029-4953
R&D Projects: GA ČR GA202/00/1425
Institutional research plan: CEZ:AV0Z1010914
Keywords : thermoluminescence * photoluminescence * potassium tantalate * photoinduced defects
Subject RIV: BM - Solid Matter Physics ; Magnetism
Impact factor: 0.290, year: 2002

After an exposure to ultraviolet light (.lambda.<350 nm) at 12 K, weak thermoluminescence of nominally pure KTaO₃ crystals was observed within the temperature region from 13 to 65K. Three glow peaks near 26,31, and 58K at the heating of 0.155K/s correspond to thermoluminescence spectrally very similar to broad-band visible photoluminescence

Po expozici ultrafialovým světlem(.lambda.<350 nm) při 12 K byla pozorována slabá termoluminiscence nominálně čistých krystalů KTaO₃ v teplotní oblasti od 13 do 65 K. Tři termoluminiscenční pásy v blízkosti 26, 31 a 58K při rychlosti ohřevu 0,155K/s odpovídají termoluminiscenci spektrálně velmi podobné širokopásmové viditelné fotoluminiscenci