Subgrain boundaries in ECAP aluminium

0095615 - ÚFM 2008 RIV CH eng J - Journal Article
Saxl, Ivan - Sklenička, Václav - Ilucová, Lucia - Svoboda, Milan - Král, Petr
Subgrain boundaries in ECAP aluminium.
[Subhranice v ultrajemnozrnném hliníku připraveném metodou ECAP.]
Materials Science Forum. Roč. 561-565, - (2007), s. 813-816. ISSN 0255-5476
R&D Projects: GA AV ČR(CZ) IAA2041301; GA ČR(CZ) GA201/06/0302
Institutional research plan: CEZ:AV0Z10190503; CEZ:AV0Z20410507
Keywords : anisotropy * ECAP * grain size
Subject RIV: BM - Solid Matter Physics ; Magnetism
Impact factor: 0.399, year: 2005

The effect of ECAP technology on the subgrain structure of coarse-grained pure aluminium is described by means of the orientation imaging microscopy (the selected lower bounds of misorientation (disclination) are 2, 5, 10 and 15 degrees). Standard profile and intercept counts carried out in three suitably oriented and mutually perpendicular section planes and along 18 systematically oriented directions, resp., are used to examine the subgrain and grain structures after the number of passes N = 2, 4, 8, 12 as well the effect of subsequent annealing (several hours at 473K). The local and overall non-homogeneity and anisotropy of boundary structures have also been evaluated.

Byl zkoumán vliv technologie ECAP na strukturu subzrn hrubozrnného čistého hliníku. K popisu struktury subzrn a zrn po 2, 4, 8 a 12 průchodech byly použity standardní profily určené ve třech vhodně orientovaných a vzájemně kolmých řezech a počty průsečíků podél 18 systematicky orientovaných směrů. Zkoumán byl také vliv následného žíhání na 473K. Dále byla určena místní a celková nehomogenita a anizotropie struktury hranic.