A route to MFI zeolite-.alpha.-alumina composite membranes for separation of light paraffins

0088797 - ÚFCH JH 2008 RIV DE eng C - Conference Paper (international conference)
Hrabánek, Pavel - Zikánová, Arlette - Bernauer, B. - Fíla, V. - Kočiřík, Milan
A route to MFI zeolite-.alpha.-alumina composite membranes for separation of light paraffins.
[Cesta k zeolitické MFI -alfa-alumina kompositní membráně pro separaci lehkých parafinů.]
Proceedings. Aachen: IVT, 2007, s. 167-172.
[Aachener Membran Kolloguium /11./. Aachen (CZ), 28.03.2007-29.03.2007]
R&D Projects: GA ČR GA203/05/0347; GA ČR GA203/07/1443; GA AV ČR IAA400400501
Institutional research plan: CEZ:AV0Z40400503
Keywords : zeolites * .alpha.-alumina composite membranes * physical chemistry
Subject RIV: CF - Physical ; Theoretical Chemistry

Silicalite-1 crystal layers were grown on ceramic asymetric porous supports. A continuous zeolite layer was prepared using a synthesis mixture aged for more than 3 days. The size of silicalite-1 crystals in a layer strongly decreased with increasing ageing period. High separation factor (> 10) for a mixture of butane isomers proved very good quality of composite membrane CM7 can be changed and influenced by temperature to find a compromise between permeation and separation.

Silikalitové krystalické vrstvy byly syntetizovány na asymetrických porézních nosičích. Kontinuální zeolitická vrstva byla připravena s použitím syntézní vsádky, která byla zrána po dobu delší než 3 dny. Velikost krystalů silikalitu-1 ve vrstvě se výrazně snížila se vzrůstající dobou zrání. Vysoký separační faktor (> 10) pro směs izomérů butanu potvrzuje kvalitní kompozitní membránu CM7. Separační vlastnosti silikalitové kompozitní membrány mohou být změněny a ovlivněny teplotou pro optimální nastavení mezi permeancí a separací.