Effect of mean stress on high-cycle fatigue strength of IN 713LC superalloy

0047067 - ÚFM 2007 RIV SK eng J - Journal Article
Kunz, Ludvík - Lukáš, Petr - Mintách, Rastislav - Hrbáček, K.
Effect of mean stress on high-cycle fatigue strength of IN 713LC superalloy.
[Vliv středního napětí na vysokocyklovou únavovou pevnost superslitiny IN 713LC.]
Kovové materiály. Roč. 44, č. 5 (2006), s. 275-281. ISSN 0023-432X. E-ISSN 1338-4252
R&D Projects: GA ČR GA106/05/2112
Institutional research plan: CEZ:AV0Z20410507
Keywords : IN 713LC * high-cycle fatigue * constant fatigue life diagram
Subject RIV: JG - Metallurgy
Impact factor: 1.138, year: 2006

Fatigue strength of Ni base superalloy IN 713LC was experimentally determined at 800 °C in air using load controlled cycling with tensile mean stress. The constant fatigue life diagram has been constructed with particular attention to the influence of small stress amplitudes at high mean stresses. The mechanism of Stage I initiation of fatigue cracks, the role of casting defects and cavities and their effect on the fatigue strength have been discussed.

Experimentálně byla stanovena únavová pevnost niklové superslitiny IN 713LC při 800°C na vzduchu při zatěžování v řízené síle a za působení tahových středních napětí. Byl zkonstruován diagram konstantní únavové životnosti se zvláštním zřetelem na vliv malých amplitud zatěžování při vysokých středních napětích. Byl diskutován mechanizmus iniciace únavových trhlin (Stage I), úloha licích defektů a kavit a jejich vliv na únavovou pevnost.