Degradation of PET, PEEK and PI induced by irradiation with 150 keV Ar+ and 1.76 MeV He+ ions

0029212 - ÚJF 2006 RIV NL eng J - Journal Article
Macková, Anna - Havránek, Vladimír - Švorčík, V. - Suzuki, T. - Djourelov, N.
Degradation of PET, PEEK and PI induced by irradiation with 150 keV Ar+ and 1.76 MeV He+ ions.
[Degradace PET, PEEK a PI polymerů indukovaná ozářením 150 keV Ar+ ionty a 1.76 MeV He+ ionty.]
Nuclear Instruments & Methods in Physics Research Section B. Roč. 240, 1/2 (2005), s. 245-249. ISSN 0168-583X. E-ISSN 1872-9584
R&D Projects: GA MŠMT(CZ) OC 527.100
Institutional research plan: CEZ:AV0Z10480505
Keywords : irradiated polymers * ion beam modification * ERDA
Subject RIV: BM - Solid Matter Physics ; Magnetism
Impact factor: 1.181, year: 2005

In this work, PET was implanted with 150 keV Ar+ ions to the fluences of 10(12)-10(15) ions/cm(2), PET, PEEK and PI with 1.76 MeV He-4(+) ions to the fluences 10(13)-10(14) ions/cm(2). Structural and compositional alterations of the implanted polymers were studied using Rutherford back-scattering (RBS), elastic recoil detection analysis (ERDA), ultra-violet and visible light spectroscopy (LTV-VIS) and positron annihilation spectroscopy (PAS). The formation of a new bonds in modified polymer films are detected in proportion to the used ion dose using UV-VIS spectroscopy. For Ar+ ions and higher fluences a decline in hydrogen and oxygen content is observed.

V této práci byl PET polymer implantován 150 keV Ar+ ionty s použitými toky 10(12)-10(15) ionty/cm(2), PET, PEEK a PI s 1.76 MeV He-4(+) ionty s toky 10(13)-10(14) iontů/cm(2). Strukturální a chemické změny polymerů po implantaci byly zkoumány metodami RBS, ERDA, UV –VIS spektroskopie a positronové anihilační spektroskopie. Vytváření nových vazeb v modifikované vrstvě polymeru a odpovídající chemické změny byly zjištěny v proporcionální závislosti na výšce použité dávky ozáření ionty.