Si-O-C ceramic foams derived from polymethylphenylsiloxane precursor with starch as foaming agent

  1. 1.
    SYSNO ASEP0448254
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevSi-O-C ceramic foams derived from polymethylphenylsiloxane precursor with starch as foaming agent
    Tvůrce(i) Černý, Martin (USMH-B) RID, ORCID, SAI
    Chlup, Zdeněk (UFM-A) RID, ORCID
    Strachota, Adam (UMCH-V) RID, ORCID
    Svítilová, Jaroslava (USMH-B)
    Schweigstillová, Jana (USMH-B) RID, ORCID, SAI
    Halasová, Martina (UFM-A)
    Rýglová, Šárka (USMH-B) RID, ORCID, SAI
    Zdroj.dok.Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219
    Roč. 35, č. 13 (2015), s. 3427-3436
    Poč.str.10 s.
    Forma vydáníTištěná - P
    Jazyk dok.eng - angličtina
    Země vyd.GB - Velká Británie
    Klíč. slovapyrolysis ; ceramic foam ; precursor ; starch ; Si-O-C
    Vědní obor RIVJI - Kompozitní materiály
    Vědní obor RIV – spolupráceÚstav fyziky materiálu - Keramika, žáruvzdorné materiály a skla
    CEPGAP107/12/2445 GA ČR - Grantová agentura ČR
    Institucionální podporaUSMH-B - RVO:67985891 ; UFM-A - RVO:68081723 ; UMCH-V - RVO:61389013
    UT WOS000359029300008
    EID SCOPUS84937523126
    DOI10.1016/j.jeurceramsoc.2015.04.032
    AnotaceSi-O-C ("black glass") ceramic foam was prepared by the foaming of a preceramic polymer, polymethylphenylsiloxane resin, and by its subsequent pyrolysis conducted up to 1000 degrees C. Prior to foaming, corn starch was blended with the diluted resin, in order to achieve uniform and small-sized pores. The foaming of the polymer blend was carried out simultaneously with its crosslinldng: escaping water vapour (forming from starch) served as the blowing agent. The apparent foam density can be controlled by adjusting the foaming temperature or by varying the amount of added starch. Both ways were used to prepare foam samples with porosity in the range of 70-90%. The porosity-dependent compressive strength of these foams was found to be in the range of 1-16 MPa. (C) 2015 Elsevier Ltd. All rights reserved.
    PracovištěÚstav struktury a mechaniky hornin
    KontaktIva Švihálková, svihalkova@irsm.cas.cz, Tel.: 266 009 216
    Rok sběru2016
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.