Fibre-matrix interface development during high temperature exposition of long fibre reinforced SiOC matrix

    1.
    SYSNO ASEP0434889
    Druh ASEPC - Konferenční příspěvek (mezinárodní konf.)
    Zařazení RIVD - Článek ve sborníku
    NázevFibre-matrix interface development during high temperature exposition of long fibre reinforced SiOC matrix
    Tvůrce(i) Chlup, Zdeněk (UFM-A) RID, ORCID
    Černý, Martin (USMH-B) RID, ORCID, SAI
    Strachota, Adam (UMCH-V) RID, ORCID
    Halasová, Martina (UFM-A)
    Dlouhý, Ivo (UFM-A) RID, ORCID
    Celkový počet autorů5
    Zdroj.dok.Materials Structure and Micromechanics of Fracture VII. - Zurich : Trans Tech Publications, 2014 / Šandera P. - ISSN 1013-9826 - ISBN 978-3-03785-934-6
    Rozsah strans. 401-404
    Poč.str.4 s.
    Forma vydáníTištěná - P
    AkceMSMF 7 - International Conference on Materials Structure & Micromechanics of Fracture /7./
    Datum konání01.07.2013-03.07.2013
    Místo konáníBrno
    ZeměCZ - Česká republika
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slovaCMCs ; pyrolysis ; heat treatment ; interface
    Vědní obor RIVJI - Kompozitní materiály
    CEPGAP107/12/2445 GA ČR - Grantová agentura ČR
    ED1.1.00/02.0068 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
    Institucionální podporaUFM-A - RVO:68081723 ; USMH-B - RVO:67985891 ; UMCH-V - RVO:61389013
    UT WOS000336694400088
    EID SCOPUS84891881737
    DOI10.4028/www.scientific.net/KEM.592-593.401
    AnotaceThe fracture behaviour of long fibre reinforced composites is predetermined mainly by properties of fibre-matrix interface. The matrix prepared by pyrolysis of polysiloxane resin possesses ability to resist high temperatures without significant damage under oxidising atmosphere. The application is therefore limited by fibres and possible changes in the fibre matrix interface. The study of development of interface during high temperature exposition is the main aim of this contribution. Application of various techniques as FIB, GIS, TEM, XRD allowed to monitor microstructural changes in the interface of selected places without additional damage caused by preparation. Additionally, it was possible to obtain information about damage, the crack formation, caused by the heat treatment from the fracture mechanics point of view.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2015
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.

Přijmout všeNastaveníOdmítnout vše