Influence of the frequency and flow rate of a pulsating water jet on the wear damage of tantalum

SYSNO ASEP	0545758
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Influence of the frequency and flow rate of a pulsating water jet on the wear damage of tantalum
Tvůrce(i)	Nag, A. (IN) Hvizdoš, P. (SK) Dixit, A. R. (IN) Petrů, J. (CZ) Hloch, Sergej (UGN-S)_{RID, SAI, ORCID}
Celkový počet autorů	5
Číslo článku	203893
Zdroj.dok.	Wear. - : Elsevier - ISSN 0043-1648 Roč. 477, July 2021 (2021)
Poč.str.	10 s.
Forma vydání	Online - E
Jazyk dok.	eng - angličtina
Země vyd.	CH - Švýcarsko
Klíč. slova	tantalum ; hydrodynamic wear ; ultrasonic ; waterjet ; surface morphology
Vědní obor RIV	JR - Ostatní strojírenství
Obor OECD	Mechanical engineering
Způsob publikování	Omezený přístup
Institucionální podpora	UGN-S - RVO:68145535
UT WOS	000679170600003
EID SCOPUS	85104346368
DOI	10.1016/j.wear.2021.203893
Anotace	The present study focuses on the hydrodynamic erosion of tantalum in the form of the disintegration depth when exposed to periodic impingements of water clusters. Discrete water clusters were generated using a pulsating water jet at excitation frequencies of 20 and 40 kHz to modulate the continuous jet into a pulsating jet. The influence of the technological parameters, such as the excitation frequency (20 and 40 kHz), supply pressure (20, 30, and 40 MPa), nozzle diameter (0.3 and 0.5 mm), and time exposure (0.25–128 s), on the erosion depth of tantalum was observed. The disintegration depth trend showed a proportional nature with the number of impingements directed to the tantalum surface keeping all other technological parameters constant. An increase in the water flow rate from 0.76 l/min (p = 20 MPa, d = 0.3 mm) to 3 l/min (p = 40 MPa, d = 0.5 mm), reduces the time exposure required for the initiation of disintegration from 4 s (80,800 impingements with f = 20 kHz) to 1 s (40,600 impingements with f = 40 kHz), respectively. The effect of change in the excitation frequency from 20 to 40 kHz was observed in form of an increase in the erosion depth from 1587 to 1762 μm at p = 40 MPa, d = 0.5 mm, and t = 128 s. The surface morphology observed using scanning electron microscopy revealed erosion features, such as craters, micro-holes, surface upheaving, and tearing, on the tantalum surface. No significant change in the mean micro-hardness values were observed near the periphery of the eroded cavity as compared to original material due to high-density of tantalum which obstruct the propagation of shock waves into the material. The outcome of the study enhances the knowledge regarding the hydrodynamic erosion of high-density materials (ρ > 15 kg/mm3) in response to the water flow rate, frequency, and time exposure.
Pracoviště	Ústav geoniky
Kontakt	Lucie Gurková, lucie.gurkova@ugn.cas.cz, Tel.: 596 979 354
Rok sběru	2022
Elektronická adresa	https://www.sciencedirect.com/science/article/pii/S0043164821002829?via%3Dihub

Počet záznamů: 1