Modification of structure and surface morphology in various ZnO facets via low fluence gold swift heavy ion irradiation

  1. 1.
    SYSNO ASEP0536516
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevModification of structure and surface morphology in various ZnO facets via low fluence gold swift heavy ion irradiation
    Tvůrce(i) Jagerová, Adéla (UJF-V) ORCID
    Malinský, Petr (UJF-V) RID, ORCID
    Mikšová, Romana (UJF-V) RID, ORCID
    Lálik, Ondřej (UJF-V)
    Cutroneo, Mariapompea (UJF-V) ORCID
    Romanenko, Olexandr V. (UJF-V) ORCID
    Szokolova, K. (CZ)
    Sofer, Z. (CZ)
    Slepička, P. (CZ)
    Čízek, J. (CZ)
    Macková, Anna (UJF-V) RID, ORCID
    Celkový počet autorů11
    Zdroj.dok.Surface and Interface Analysis - ISSN 0142-2421
    Roč. 53, č. 2 (2021), s. 230-243
    Poč.str.14 s.
    Forma vydáníTištěná - P
    Jazyk dok.eng - angličtina
    Země vyd.US - Spojené státy americké
    Klíč. slovasingle ion irradiation ; swift heavy-ion irradiation ; ZnO nanostructuring
    Vědní obor RIVBG - Jaderná, atomová a mol. fyzika, urychlovače
    Obor OECDAtomic, molecular and chemical physics (physics of atoms and molecules including collision, interaction with radiation, magnetic resonances, Mössbauer effect)
    CEPLM2015056 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    EF16_013/0001812 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    GA18-03346S GA ČR - Grantová agentura ČR
    Způsob publikováníOmezený přístup
    Institucionální podporaUJF-V - RVO:61389005
    UT WOS000585037100001
    EID SCOPUS85094198191
    DOI10.1002/sia.6904
    AnotaceThe influence of low fluence high-energy ion irradiation on the modification of the ZnO surface structure and optical properties has been studied. ZnO samples of various orientations, namely, c-plane (0001), a-plane (11-20) and m-plane (10-10), have been implanted with 30-MeV Au ions with fluences ranging from 5 x 10(9) to 5 x 10(11) cm(-2). Rutherford backscattering spectrometry in the channelling mode (RBS-C) and Raman spectroscopy has shown the distinct damage accumulation in the irradiated surface layer about 1 mu m depending on the ZnO facet being to larger extent evidenced in the m-plane ZnO. Contrary, the a-plane ZnO has been exhibited the lowest Zn disorder. Using atomic force microscopy (AFM), a complex morphology was detected on the irradiated samples containing grains and exhibiting increased roughness, both growing with the Au implantation fluence mainly in m-plane ZnO. Positron annihilation spectroscopy (PAS) has shown distinct defect accumulation at the Au-ion fluence of 5 x 10(11) cm(-2), where RBS-C and Raman spectroscopy indicated sudden disorder increase in the irradiated layers, probably the creation of more complex clusters of Zn and O vacancies 4VZn + 8VO initiated in connection with an overlap of individual ion impacts. Photoluminescence measurements have shown a distinct near-band-edge (NBE) luminescence, developing with the increasing Au-ion fluence in various ZnO orientations. The m-plane ZnO had the most progressively suppressed NBE in comparison with the other orientations.
    PracovištěÚstav jaderné fyziky
    KontaktMarkéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228 ; Renata Glasová, glasova@ujf.cas.cz, Tel.: 266 177 223
    Rok sběru2022
    Elektronická adresahttps://doi.org/10.1002/sia.6904
Počet záznamů: 1