    NázevInitiation and Early Growth of Fatigue
    Cracks
    Tvůrce(i) Polák, Jaroslav (UFM-A) RID, ORCID
    Celkový počet autorů1
    Zdroj.dok.TMS 2019 148th Annual. - Cham : Springer, 2019 - ISSN 2367-1181 - ISBN 978-3-030-05861-6
    Rozsah strans. 1125-1135
    Poč.str.11 s.
    Forma vydáníTištěná - P
    AkceTMS 2019 - Annual Meeting and Exhibition of The Minerals, Metals and Materials Society /148./
    Datum konání10.03.2019 - 14.03.2019
    Místo konáníSan Antonio
    ZeměUS - Spojené státy americké
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slovaCrack initiation ; Crack growth ; Damage mechanism
    Vědní obor RIVJG - Hutnictví, kovové materiály
    Obor OECDMaterials engineering
    CEPLM2015069 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    LQ1601 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000560397400107
    EID SCOPUS85064854442
    DOI10.1007/978-3-030-05861-6_109
    AnotaceExperimental evidence concerning the mechanism of initiation and early
    growth of short cracks are studied using FESEM, FIB and STEM observations of the
    surface of fatigued specimens of several f.c.c.metals. The true shape of persistent slip
    markings with high resolution is obtained on FIB cuts and using lamella milled on the
    surface. Thick extrusions and parallel thin crack-like intrusions are typical feature
    before crack initiates from the tip of the intrusion. STEM also reveals the relation of
    the surface relief and internal structure of the material showing in copper ladder-like
    dislocation structure. The shape of the persistent slip markings is confronted with the
    predictions of the recent theoretical models. Study of the short crack growth and its
    kinetics shows high density of initiated surface cracks and proves the acceleration of
    the crack growth rate due to linkage of principal crack with initiated surface cracks.
    Fatigue life is determined by the growth of short cracks and short crack growth law
    is equivalent to the Manson–Coffin law.