Influence of sandblasting and acid etching on fatigue properties of\nultra-fine grained Ti grade 4 for dental implants

  1. 1.
    SYSNO ASEP0531638
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevInfluence of sandblasting and acid etching on fatigue properties of
    ultra-fine grained Ti grade 4 for dental implants
    Tvůrce(i) Fintová, Stanislava (UFM-A) ORCID
    Kuběna, Ivo (UFM-A) RID, ORCID
    Palán, J. (CZ)
    Mertová, K. (CZ)
    Duchek, M. (CZ)
    Hutař, Pavel (UFM-A) RID, ORCID
    Pastorek, F. (SK)
    Kunz, Ludvík (UFM-A) RID, ORCID
    Celkový počet autorů8
    Číslo článku104016
    Zdroj.dok.Journal of the Mechanical Behavior of Biomedical Materials. - : Elsevier - ISSN 1751-6161
    Roč. 111, NOV (2020)
    Poč.str.10 s.
    Jazyk dok.eng - angličtina
    Země vyd.NL - Nizozemsko
    Klíč. slovaFatigue ; CP Ti grade 4 ; UFG ; Fatigue crack initiation ; SLA
    Vědní obor RIVJG - Hutnictví, kovové materiály
    Obor OECDMaterials engineering
    CEPLQ1601 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Způsob publikováníOmezený přístup
    Institucionální podporaUFM-A - RVO:68081723
    UT WOS000575377200004
    EID SCOPUS85089275388
    DOI10.1016/j.jmbbm.2020.104016
    AnotaceCommercially pure Ti is a typical material for dental implants. Besides oral environmental effects, implants are seriously mechanically loaded during the lifetime. Mechanical resistance of coarse and ultra-fine grained Ti grade 4 was investigated. Significant grain size refinement resulting in the 65% increase of the proof stress is reported. The fatigue endurance limit increased from 523 MPa to 698 MPa due to grain refinement. The influence of sandblasting combined with acid etching on fatigue damage of both material states was analyzed. The surface treatment was proven as detrimental to the fatigue properties of both material states, due to reduction of the fatigue initiation stage. Nevertheless, the fatigue endurance limit of the surface-treated ultra-fine grained material remained higher than the fatigue endurance limit of the coarse-grained material without surface treatment. Reported results confirm better mechanical resistance of ultra-fine grained materials for dental implants in the comparison with coarse-grain one.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2021
    Elektronická adresahttps://www.sciencedirect.com/science/article/pii/S1751616120305671?via%3Dihub
Počet záznamů: 1