Phase, composition and structure changes of CoCrNi-based concentrated alloys resulting from high temperature oxidation
- 1.
SYSNO ASEP 0531256 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Phase, composition and structure changes of CoCrNi-based concentrated alloys resulting from high temperature oxidation Tvůrce(i) Vilémová, Monika (UFP-V) RID, ORCID
Hadraba, Hynek (UFM-A) RID, ORCID
Weiss, Zdeněk (FZU-D) ORCID
Lukáč, František (UFP-V) ORCID
Csáki, Štefan (UFP-V) ORCID
Chlup, Zdeněk (UFM-A) RID, ORCID
Matějíček, Jiří (UFP-V) RID, ORCID
Chráska, Tomáš (UFP-V) RID, ORCIDCelkový počet autorů 8 Číslo článku 2276 Zdroj.dok. Materials. - : MDPI
Roč. 13, č. 10 (2020)Poč.str. 13 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova Cr C dissolution 23 6 ; CrMnFeCoNi ; FeCoNiCr ; High-entropy alloys ; Medium-entropy alloys ; Oxide dispersion strengthening ; Passivation ; Spark plasma sintering ; Y-Ti complex oxide nanoparticles ; Y O particles 2 3 Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Vědní obor RIV – spolupráce Fyzikální ústav - Fyzika pevných látek a magnetismus
Ústav fyziky materiálu - Hutnictví, kovové materiályCEP GA17-23964S GA ČR - Grantová agentura ČR EF16_019/0000760 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Způsob publikování Open access Institucionální podpora UFP-V - RVO:61389021 ; FZU-D - RVO:68378271 ; UFM-A - RVO:68081723 UT WOS 000539277000068 EID SCOPUS 85085600793 DOI 10.3390/ma13102276 Anotace In this work, CoCrNi, FeCoCrNi and CoCrFeMnNi concentrated alloys with a Y-Ti oxide particle dispersion were prepared by mechanical alloying and Spark Plasma Sintering. The alloy consists of an FCC Ni-based matrix with a Y-Ti oxide dispersion and additional phases of Cr23C6 and Cr2O3. The effect of Fe, Mn, and Y-Ti oxide particles on the formation of oxide scales and the composition of the adjacent CoCrNi and FeCoCrNi alloys was studied. It was found that alloys without Mn in their composition form a protective Cr2O3 scale. The Cr23C6 particles provide an alternative mechanism for balancing the chromium loss during the oxidation. Y and Ti from the oxide particles participate in the formation of the protective oxide scales. Fe promotes Y and especially Ti diffusion through the Cr2O3 scale, resulting in the formation of Ti-depleted regions in the alloy. The findings will serve for the further development of these new materials. Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2021 Elektronická adresa https://www.mdpi.com/1996-1944/13/10/2276