Phase, composition and structure changes of CoCrNi-based concentrated alloys resulting from high temperature oxidation

  1. 1.
    SYSNO ASEP0531256
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevPhase, composition and structure changes of CoCrNi-based concentrated alloys resulting from high temperature oxidation
    Tvůrce(i) Vilémová, Monika (UFP-V) RID, ORCID
    Hadraba, Hynek (UFM-A) RID, ORCID
    Weiss, Zdeněk (FZU-D) ORCID
    Lukáč, František (UFP-V) ORCID
    Csáki, Štefan (UFP-V) ORCID
    Chlup, Zdeněk (UFM-A) RID, ORCID
    Matějíček, Jiří (UFP-V) RID, ORCID
    Chráska, Tomáš (UFP-V) RID, ORCID
    Celkový počet autorů8
    Číslo článku2276
    Zdroj.dok.Materials. - : M D P I AG
    Roč. 13, č. 10 (2020)
    Poč.str.13 s.
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slovaCr C dissolution 23 6 ; CrMnFeCoNi ; FeCoNiCr ; High-entropy alloys ; Medium-entropy alloys ; Oxide dispersion strengthening ; Passivation ; Spark plasma sintering ; Y-Ti complex oxide nanoparticles ; Y O particles 2 3
    Vědní obor RIVJG - Hutnictví, kovové materiály
    Obor OECDMaterials engineering
    Vědní obor RIV – spolupráceFyzikální ústav - Fyzika pevných látek a magnetismus
    Ústav fyziky materiálu - Hutnictví, kovové materiály
    CEPGA17-23964S GA ČR - Grantová agentura ČR
    EF16_019/0000760 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Způsob publikováníOpen access
    Institucionální podporaUFP-V - RVO:61389021 ; FZU-D - RVO:68378271 ; UFM-A - RVO:68081723
    UT WOS000539277000068
    EID SCOPUS85085600793
    DOI10.3390/ma13102276
    AnotaceIn this work, CoCrNi, FeCoCrNi and CoCrFeMnNi concentrated alloys with a Y-Ti oxide particle dispersion were prepared by mechanical alloying and Spark Plasma Sintering. The alloy consists of an FCC Ni-based matrix with a Y-Ti oxide dispersion and additional phases of Cr23C6 and Cr2O3. The effect of Fe, Mn, and Y-Ti oxide particles on the formation of oxide scales and the composition of the adjacent CoCrNi and FeCoCrNi alloys was studied. It was found that alloys without Mn in their composition form a protective Cr2O3 scale. The Cr23C6 particles provide an alternative mechanism for balancing the chromium loss during the oxidation. Y and Ti from the oxide particles participate in the formation of the protective oxide scales. Fe promotes Y and especially Ti diffusion through the Cr2O3 scale, resulting in the formation of Ti-depleted regions in the alloy. The findings will serve for the further development of these new materials.