Fatigue behavior of AW7075 aluminum alloy in ultra-high cycle fatigue region

SYSNO ASEP	0523973
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Fatigue behavior of AW7075 aluminum alloy in ultra-high cycle fatigue region
Tvůrce(i)	Fintová, Stanislava (UFM-A)_ORCID Kuběna, Ivo (UFM-A)_{RID, ORCID} Trško, L. (SK) Horník, Vít (UFM-A) Kunz, Ludvík (UFM-A)_{RID, ORCID}
Celkový počet autorů	5
Číslo článku	138922
Zdroj.dok.	Materials Science and Engineering A Structural Materials Properties Microstructure and Processing. - : Elsevier - ISSN 0921-5093 Roč. 774, FEB (2020)
Poč.str.	8 s.
Jazyk dok.	eng - angličtina
Země vyd.	CH - Švýcarsko
Klíč. slova	precipitate-free zones ; anodic-oxidation ; mechanisms ; performance ; damage ; life ; Fatigue ; Ultra-high cycle fatigue ; Fatigue crack initiation ; Fatigue damage ; aw7075
Vědní obor RIV	JG - Hutnictví, kovové materiály
Obor OECD	Materials engineering
CEP	EF16_013/0001823 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
Způsob publikování	Omezený přístup
Institucionální podpora	UFM-A - RVO:68081723
UT WOS	000514747200013
EID SCOPUS	85077674805
DOI	10.1016/j.msea.2020.138922
Anotace	Advanced electron microscopy methods were used with the aim to explain the differences in the response of strengthened AW 7075 T6511 aluminum alloy to fatigue loading at 5 Hz and 20 kHz. The shift of the S-N curve to higher number of cycles to fracture for the specimens tested at high frequency was experimentally determined. This effect is not connected with a change of the fatigue crack initiation mechanism and site from the surface to material interior. The absence of slip markings and cracking of primary intermetallic particles on the surface of cycled specimens were characteristic features. A difference in the dislocation density and dislocation arrangement in the vicinity of the fatigue crack initiation sites was shown to be the only observable effect. However, consistent with the strengthened structure of the alloy, no specific dislocation structure due to the cyclic loading was observed, regardless of the loading frequency and stress amplitude.