Fatigue Behaviour and Crack Initiation in CoCrFeNiMn High-Entropy Alloy Processed by Powder Metallurgy

  1. 1.
    SYSNO ASEP0510156
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevFatigue Behaviour and Crack Initiation in CoCrFeNiMn High-Entropy Alloy Processed by Powder Metallurgy
    Tvůrce(i) Chlup, Zdeněk (UFM-A) RID, ORCID
    Fintová, Stanislava (UFM-A) ORCID
    Hadraba, Hynek (UFM-A) RID, ORCID
    Kuběna, Ivo (UFM-A) RID, ORCID
    Vilémová, Monika (UFP-V) RID, ORCID
    Matějíček, Jiří (UFP-V) RID, ORCID
    Celkový počet autorů6
    Číslo článku1110
    Zdroj.dok.Metals
    Roč. 9, č. 10 (2019)
    Poč.str.11 s.
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slovahigh entropy alloy ; microstructure ; spark plasma sintering ; fatigue ; grain size
    Vědní obor RIVJG - Hutnictví, kovové materiály
    Obor OECDMaterials engineering
    Vědní obor RIV – spolupráceÚstav fyziky plazmatu
    CEPGA17-23964S GA ČR - Grantová agentura ČR
    Způsob publikováníOpen access
    Institucionální podporaUFM-A - RVO:68081723 ; UFP-V - RVO:61389021
    UT WOS000498219400089
    EID SCOPUS85074239473
    DOI10.3390/met9101110
    AnotaceOxide dispersion-strengthened (ODS) materials contain homogeneous dispersions of temperature-stable nano-oxides serving as obstacles for dislocations and further pinning of grain boundaries. The strategy for dispersion strengthening based on complex oxides (Y-Hf, -Zr, -Ce, -La) was developed in order to refine oxide dispersion to enhance the dispersion strengthening effect. In this work, the strengthening of EUROFER steel by complex oxides based on Y and elements of the IIIB group (lanthanum, scandium) and IVB group (cerium, hafnium, zirconium) was explored. Interparticle spacing as a dispersoid characteristic appeared to be an important factor in controlling the dispersion strengthening contribution to the yield strength of ODS EUROFER steels. The dispersoid size and average grain size of ODS EUROFER steel were altered in the ranges of 5–13 nm and 0.6–1.7 m, respectively. Using this strategy, the yield strength of the prepared alloys varied between 550 MPa and 950 MPa depending on the doping element.