Fatigue Behaviour and Crack Initiation in CoCrFeNiMn High-Entropy Alloy Processed by Powder Metallurgy
- 1.
SYSNO ASEP 0510156 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Fatigue Behaviour and Crack Initiation in CoCrFeNiMn High-Entropy Alloy Processed by Powder Metallurgy Tvůrce(i) Chlup, Zdeněk (UFM-A) RID, ORCID
Fintová, Stanislava (UFM-A) ORCID
Hadraba, Hynek (UFM-A) RID, ORCID
Kuběna, Ivo (UFM-A) RID, ORCID
Vilémová, Monika (UFP-V) RID, ORCID
Matějíček, Jiří (UFP-V) RID, ORCIDCelkový počet autorů 6 Číslo článku 1110 Zdroj.dok. Metals. - : MDPI
Roč. 9, č. 10 (2019)Poč.str. 11 s. Jazyk dok. eng - angličtina Země vyd. CH - Švýcarsko Klíč. slova high entropy alloy ; microstructure ; spark plasma sintering ; fatigue ; grain size Vědní obor RIV JG - Hutnictví, kovové materiály Obor OECD Materials engineering Vědní obor RIV – spolupráce Ústav fyziky plazmatu CEP GA17-23964S GA ČR - Grantová agentura ČR Způsob publikování Open access Institucionální podpora UFM-A - RVO:68081723 ; UFP-V - RVO:61389021 UT WOS 000498219400089 EID SCOPUS 85074239473 DOI 10.3390/met9101110 Anotace Oxide dispersion-strengthened (ODS) materials contain homogeneous dispersions of temperature-stable nano-oxides serving as obstacles for dislocations and further pinning of grain boundaries. The strategy for dispersion strengthening based on complex oxides (Y-Hf, -Zr, -Ce, -La) was developed in order to refine oxide dispersion to enhance the dispersion strengthening effect. In this work, the strengthening of EUROFER steel by complex oxides based on Y and elements of the IIIB group (lanthanum, scandium) and IVB group (cerium, hafnium, zirconium) was explored. Interparticle spacing as a dispersoid characteristic appeared to be an important factor in controlling the dispersion strengthening contribution to the yield strength of ODS EUROFER steels. The dispersoid size and average grain size of ODS EUROFER steel were altered in the ranges of 5–13 nm and 0.6–1.7 m, respectively. Using this strategy, the yield strength of the prepared alloys varied between 550 MPa and 950 MPa depending on the doping element. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2020 Elektronická adresa https://www.mdpi.com/2075-4701/9/10/1110/htm
Počet záznamů: 1