Deconstruction of microfibrillated cellulose into nanocrystalline cellulose rods and mesogenic phase formation in concentrated low-modulus sodium silicate solutions

SYSNO ASEP	0504757
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Deconstruction of microfibrillated cellulose into nanocrystalline cellulose rods and mesogenic phase formation in concentrated low-modulus sodium silicate solutions
Tvůrce(i)	Bertolla, Luca (UFM-A)_ORCID Dlouhý, Ivo (UFM-A)_{RID, ORCID} Bartoníčková, E. (CZ) Toušek, J. (CZ) Nováček, J. (CZ) Mácová, Petra (UTAM-F)_{RID, SAI, ORCID}
Celkový počet autorů	6
Zdroj.dok.	Cellulose. - : Springer - ISSN 0969-0239 Roč. 26, č. 7 (2019), s. 4325-4344
Poč.str.	20 s.
Jazyk dok.	eng - angličtina
Země vyd.	NL - Nizozemsko
Klíč. slova	Microfibrillated cellulose ; Cellulose nanocrystal ; Sodium silicate
Vědní obor RIV	JH - Keramika, žáruvzdorné materiály a skla
Obor OECD	Ceramics
Vědní obor RIV – spolupráce	Ústav teoretické a aplikované mechaniky - Keramika, žáruvzdorné materiály a skla
CEP	LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
Způsob publikování	Omezený přístup
Institucionální podpora	UFM-A - RVO:68081723 ; UTAM-F - RVO:68378297
UT WOS	000465576000008
EID SCOPUS	85064180245
DOI	10.1007/s10570-019-02364-6
Anotace	This work demonstrates for the first time the deconstruction of microfibrillated cellulose (MFC) into rod-like cellulose nanocrystals (CNCs) in concentrated low modulus sodium silicate solutions. To this aim, MFC suspensions at different concentrations were first treated in sodium hydroxide solutions and then amorphous silica powder was added. Optical microscopy and transmission electron microscopy observation showed how MFC was efficiently deconstructed into CNCs, evidencing the occurrence of a phase separation into an isotropic and mesogenic phase. The extracted CNCs were characterized by a remarkably higher length (600-1200nm) in comparison with the plant-derived ones commonly reported in literature. FT-IR spectroscopy and Si-29 MAS NMR confirmed that the Q(n) equilibrium of the suspended silicate species was affected, proportionally to the amount of MFC. It was also shown, that due to the excluded volume effect exerted by silicate anions, nematic or smectic ordering could be achieved for CNC concentrations far below the critical rod concentration predicted by the Doi-Edwards model.
Pracoviště	Ústav fyziky materiálu
Kontakt	Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
Rok sběru	2020
Elektronická adresa	https://link.springer.com/article/10.1007/s10570-019-02364-6