Dilatometric study of anisotropic sintering of alumina/zirconia laminates with controlled fracture behaviour
- 1.
SYSNO ASEP 0480425 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Dilatometric study of anisotropic sintering of alumina/zirconia laminates with controlled fracture behaviour Tvůrce(i) Maca, K. (CZ)
Pouchlý, V. (CZ)
Drdlík, D. (CZ)
Hadraba, Hynek (UFM-A) RID, ORCID
Chlup, Zdeněk (UFM-A) RID, ORCIDCelkový počet autorů 5 Zdroj.dok. Journal of the European Ceramic Society. - : Elsevier - ISSN 0955-2219
Roč. 37, č. 14 (2017), s. 4287-4295Poč.str. 9 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova Alumina/zirconia laminate ; Crack deflection ; Master sintering curve ; Sintering shrinkage Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla Obor OECD Ceramics CEP GA15-06390S GA ČR - Grantová agentura ČR LQ1601 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy Institucionální podpora UFM-A - RVO:68081723 UT WOS 000408178300007 EID SCOPUS 85018730360 DOI 10.1016/j.jeurceramsoc.2017.04.030 Anotace Al2O3 and ZrO2 monoliths as well as layered Al2O3/ZrO2 composites with a varying layer thickness ratio were prepared by electrophoretic deposition. The sintering shrinkage of these materials in the transversal (perpendicular to the layers, i.e. in the direction of deposition) as well as in the longitudinal (parallel with layers interfaces) direction were monitored using high-temperature dilatometry. The sintering of layered composites exhibited anisotropic behaviour. The detailed study revealed that sintering shrinkage in the longitudinal direction was governed by alumina (material with a higher sintering temperature), whilst in the transversal direction it was accelerated by the directional sintering of zirconia layers. For interpretation of such anisotropic sintering kinetics, the Master Shrinkage Curve model was developed and applied. Crack propagation through laminates with a different alumina/zirconia thickness ratio was described with the help of scanning electron microscopy and confocal laser microscopy. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2018
Počet záznamů: 1