Fracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead

  1. 1.
    SYSNO ASEP0480409
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevFracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead
    Tvůrce(i) Hojná, A. (CZ)
    Di Gabriele, F. (CZ)
    Hadraba, Hynek (UFM-A) RID, ORCID
    Husák, Roman (UFM-A)
    Kuběna, Ivo (UFM-A) RID, ORCID
    Rozumová, L. (CZ)
    Bublíková, P. (CZ)
    Kalivodová, J. (CZ)
    Matějíček, Jiří (UFP-V) RID, ORCID
    Celkový počet autorů9
    Zdroj.dok.Journal of Nuclear Materials. - : Elsevier - ISSN 0022-3115
    Roč. 490, JUL (2017), s. 143-154
    Poč.str.12 s.
    Jazyk dok.eng - angličtina
    Země vyd.NL - Nizozemsko
    Klíč. slovaImpact fracture ; Microanalysis ; Nanostructured steel ; Oxidation ; Thermal ageing
    Vědní obor RIVJG - Hutnictví, kovové materiály
    Obor OECDMaterials engineering
    Vědní obor RIV – spolupráceÚstav fyziky plazmatu - Hutnictví, kovové materiály
    CEPGA14-25246S GA ČR - Grantová agentura ČR
    GA14-12837S GA ČR - Grantová agentura ČR
    LQ1601 GA MŠk - Ministerstvo školství, mládeže a tělovýchovy
    Institucionální podporaUFM-A - RVO:68081723 ; UFP-V - RVO:61389021
    UT WOS000403132300017
    EID SCOPUS85018463374
    DOI10.1016/j.jnucmat.2017.03.049
    AnotaceThis work describes the fracture behaviour of the 14Cr ODS steel produced by mechanical alloying process, after high temperature exposures. Small specimens were exposed to helium gas in a furnace at 720 degrees C for 500 h. Another set of specimens was exposed to flowing liquid lead in the COLONRI II loop at 650 degrees C for 1000 h. All specimens were tested for the impact and tensile behaviour. The impact test results are compared to other sets of specimens in the as received state and after isothermal annealing at 650 degrees C for 1000 h. The impact curves of the exposed materials showed positive shifts on the transition temperature. While the upper shelf value did not change in the Pb exposed ODS steel, it significantly increased in the He exposed one. The differences are discussed in terms of surface and subsurface microscopy observation. The embrittlement can be explained as the effect of a slight change in the grain boundary and size distribution combined with the depletion of sub-surface region from alloying elements forming oxide scale on the surface.