Behavior and microstructural changes in different tungsten-based materials under pulsed plasma loading

  1. 1.
    SYSNO ASEP0468206
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevBehavior and microstructural changes in different tungsten-based materials under pulsed plasma loading
    Tvůrce(i) Vilémová, Monika (UFP-V) RID, ORCID
    Pala, Zdeněk (UFP-V) RID
    Jäger, Aleš (FZU-D) RID, ORCID
    Matějíček, Jiří (UFP-V) RID, ORCID
    Chernyshova, M. (PL)
    Kowalska-Strzeciwilk, E. (PL)
    Gribkov, V. A. (PL)
    Janata, Marek (UFP-V)
    Zdroj.dok.Nuclear Materials and Energy - ISSN 2352-1791
    Roč. 9, December (2016), s. 123-127
    Poč.str.5 s.
    Forma vydáníTištěná - P
    AkceInternational Conference of Fusion Reactor Material (ICFRM-17) /17./
    Datum konání11.10.2015 - 16.10.2015
    Místo konáníAachen
    ZeměDE - Německo
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.NL - Nizozemsko
    Klíč. slovaODS tungsten ; yttrium oxide ; porosity ; phase stability ; monoclinic phase ; plasma focus ; damage ; erosion
    Vědní obor RIVJJ - Ostatní materiály
    Vědní obor RIV – spolupráceFyzikální ústav - Ostatní materiály
    CEPGA14-12837S GA ČR - Grantová agentura ČR
    Institucionální podporaUFP-V - RVO:61389021 ; FZU-D - RVO:68378271
    UT WOS000391191500020
    EID SCOPUS85006802843
    DOI10.1016/j.nme.2016.06.004
    AnotaceIn this study, morphological, microstructural and phase changes of four types of tungsten materials after exposure to dense deuterium plasma were examined. The microstructures of the prepared materials mutually differ by the porosity, grain size and phase content. It was found that inherent porosity of sintered materials leads to a specific mechanism of erosion and might be a significant source of dust in the case of materials with higher porosity. Further, a preferential erosion of the dispersed particles by melting and evaporation and subsequent formation of thin film on the surface of W-Y2O3 was described as well.