The influence of processing temperature and the starch content on the microstructure and mechanical properties of SiOC foams

SYSNO ASEP	0450445
Druh ASEP	A - Abstrakt
Zařazení RIV	Není vybrán druh dokumentu
Název	The influence of processing temperature and the starch content on the microstructure and mechanical properties of SiOC foams
Tvůrce(i)	Halasová, Martina (UFM-A) Černý, Martin (USMH-B)_{RID, ORCID, SAI} Chlup, Zdeněk (UFM-A)_{RID, ORCID} Strachota, Adam (UMCH-V)_{RID, ORCID} Dlouhý, Ivo (UFM-A)_{RID, ORCID}
Celkový počet autorů	5
Zdroj.dok.	Book of Abstracts. 17th International Conference on the Strength of Materials (ICSMA-17). - Brno : Ústav fyziky materiálů AV ČR, v. v. i., 2015 / Dlouhý A. ; Kunz L. - ISBN 978-80-87434-07-9 S. 301
Poč.str.	1 s.
Akce	ICSMA-17 International Conference on the Strength of Materials /17./
Datum konání	09.08.2015-14.08.2015
Místo konání	Brno
Země	CZ - Česká republika
Typ akce	WRD
Jazyk dok.	eng - angličtina
Země vyd.	CZ - Česká republika
Klíč. slova	SiOC glass ; Foams ; mechanical properties
Vědní obor RIV	JL - Únava materiálu a lomová mechanika
Vědní obor RIV – spolupráce	Ústav makromolekulární chemie - Makromolekulární chemie Ústav struktury a mechaniky hornin - Únava materiálu a lomová mechanika
Institucionální podpora	UFM-A - RVO:68081723 ; USMH-B - RVO:67985891 ; UMCH-V - RVO:61389013
Anotace	The SiOC foams were prepared from polymethylphenylsiloxane resin (commercially known as L901 resin) and a commonly available starch as a foaming agent. A set of specimens of various starch content and the processing temperature to find the optimum combination and as well as the dependences allowing tailoring of materials were prepared. The optimum amount of starch was elaborated at the temperature of 230 °C and the amount of the starch varied from 0.7 up to 2.2 wt%. The specimens were processed at the temperature range from 220 to 250 °C with the step of 10 °C to observe the influence of temperature on the gas evolution and therefore the structure development of foam for constant amount of foaming agent at the level of 2 wt/%. Theoretical and relative foam densities were calculated based on the known bulk SiOC density after pyrolysis (1.8 g