SYSNO ASEP	0445134
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Comparative analysis of thermal stability of two different nc-TiC/a-C:H coatings
Tvůrce(i)	Zábranský, L. (CZ) Buršíková, V. (CZ) Daniel, L. (CZ) Souček, P. (CZ) Vašina, P. (CZ) Dugáček, J. (CZ) Sťahel, P. (CZ) Caha, O. (CZ) Buršík, Jiří (UFM-A)_{RID, ORCID} Peřina, Vratislav (UJF-V)_RID
Celkový počet autorů	10
Zdroj.dok.	Surface and Coatings Technology. - : Elsevier - ISSN 0257-8972 Roč. 267, APR (2015), s. 32-39
Poč.str.	8 s.
Jazyk dok.	eng - angličtina
Země vyd.	CH - Švýcarsko
Klíč. slova	nanocomposite ; thermal annealing ; hardness
Vědní obor RIV	BM - Fyzika pevných látek a magnetismus
Vědní obor RIV – spolupráce	Ústav jaderné fyziky - Jaderná, atomová a mol. fyzika, urychlovače
CEP	LM2011019 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
Institucionální podpora	UFM-A - RVO:68081723 ; UJF-V - RVO:61389005
UT WOS	000353845700006
EID SCOPUS	84925942739
DOI	10.1016/j.surfcoat.2015.01.058
Anotace	The aim of this work is to compare the thermal stability of two nanocrystalline TiC/a-C:H coatings prepared by magnetron sputtering of titanium target in acetylene containing environment. The coatings exhibited different chemical composition ([Ti]/[C] ratio) and structure. Their thermal stability was studied using thermal desorption spectroscopy in the temperature range from 500 to 1000 °C. The hardness and elastic modulus of both coatings remained almost unchanged up to 700 °C, however, they substantially differed from the point of view of their fracture resistance. Up to 700 °C no indentation induced cracking occurred in the titanium rich coating, however, reaching the annealing temperature of 1000 °C, this coating became porous and spontaneous tensile cracking appeared on its surface.