Designing (Al-)SBA-15 Catalyst Pellet with Unique Properties

SYSNO ASEP	0356437
Druh ASEP	C - Konferenční příspěvek (mezinárodní konf.)
Zařazení RIV	D - Článek ve sborníku
Název	Designing (Al-)SBA-15 Catalyst Pellet with Unique Properties
Tvůrce(i)	Topka, Pavel (UCHP-M)_{RID, ORCID, SAI} Zub, Yu.L. (UA) Karban, Jindřich (UCHP-M)_{RID, ORCID, SAI} Šolcová, Olga (UCHP-M)_{RID, ORCID, SAI}
Zdroj.dok.	Characterisation of Porous Solids VIII. - Cambridge : Royal Society of Chemistry Publishing, 2009 / Kaskel S. ; Llewellyn P. ; Rodriguez-Reinoso F. ; Seaton N.A. - ISSN 0260-6291 - ISBN 978-1-84755-904-3
Rozsah stran	s.287-294
Poč.str.	8 s.
Akce	International Symposium on the Characterization of Porous Solids /8./
Datum konání	10.06.2008-13.06.2008
Místo konání	Edinburg
Země	GB - Velká Británie
Typ akce	WRD
Jazyk dok.	eng - angličtina
Země vyd.	GB - Velká Británie
Klíč. slova	catalyst pellet ; mesoporous molecular sieves ; mesoporous silica
Vědní obor RIV	CA - Anorganická chemie
CEP	IAA4072404 GA AV ČR - Akademie věd
	KAN400720701 GA AV ČR - Akademie věd
CEZ	AV0Z40720504 - UCHP-M (2005-2011)
UT WOS	000269656900038
Anotace	Self-supporting pellets were successfully formed from SBA-15 and Al-SBA-15 powder without the addition of binder or plasticizer. Prepared self-supporting pellets maintained the porous structure of original powder. In comparison with parent sample, a decrease of mesopore surface area and mesopore volume up to 40 % was noticed in the case of pellets formed with the highest 17.7 MPa pressure. The Al-SBA-15 pellets prepared using 4.7 MPa forming pressure were enough mechanically stable to retain the structural integrity during batch alkylation of toluene with benzyl alcohol at 110 °C. The conversion reached with Al-SBA-15 pellets after 60 min of the reaction was about five times lower than that accomplished with powder Al-SBA-15.