Comparison of low cycle fatigue of ductile cast irons with different matrix alloyed with nickel
- 1.
SYSNO ASEP 0355181 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Comparison of low cycle fatigue of ductile cast irons with different matrix alloyed with nickel Tvůrce(i) Petrenec, Martin (UFM-A)
Tesařová, H. (CZ)
Beran, Přemysl (UJF-V) RID, ORCID, SAI
Šmíd, Miroslav (UFM-A) RID, ORCID
Roupcová, Pavla (UFM-A) RID, ORCIDZdroj.dok. Procedia Engineering. - Amsterdam : Elsevier BV
Roč. 2, č. 1 (2010), s. 2307-2316Poč.str. 10 s. Akce Fatigue 2010 Datum konání 06.06.2010-11.06.2010 Místo konání Praha Země CZ - Česká republika Typ akce WRD Jazyk dok. eng - angličtina Země vyd. NL - Nizozemsko Klíč. slova Low cycle fatigue ; ferritic ductile cast iron ; ADI ; nickel alloying ; neutron diffraction Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GAP108/10/2371 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) AV0Z10480505 - UJF-V (2005-2011) UT WOS 000278762900245 DOI 10.1016/j.proeng.2010.03.247 Anotace Total strain controlled tests have been performed on cylindrical specimens of austempered ductile cast iron (ADI) and ductile cast iron with the ferritic matrix, both alloyed with 2.75% Ni, with the aim to compare cyclic plasticity and the fatigue life at temperatures 23 °C and–45 °C.In ADI the measurement of retained austenite by neutron diffraction before and after fatigue tests is used to discuss the cyclic stress-strain response. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained for both temperatures and materials. Cyclic stress-strain curve obtained at–45 °C is shifted to higher stress amplitudes relative to room temperature curve. The Manson-Coffin curves are identical for both materials and temperatures while the Basquin curve is shifted to longer fatigue life for ADI. The surface relief developed during fatigue was studied using SEM. Fatigue cracks initiated preferably from persistent slip markings at the interface of graphite nodule. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2011
Počet záznamů: 1