Mössbauer Effect Study Of Iron Thin Films On Si/SiOx Substrate And Iron Phases At Deposited Carbon Nanotubes
- 1.
SYSNO ASEP 0354513 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Mössbauer Effect Study Of Iron Thin Films On Si/SiOx Substrate And Iron Phases At Deposited Carbon Nanotubes Tvůrce(i) Schneeweiss, Oldřich (UFM-A) RID, ORCID
David, Bohumil (UFM-A) RID
Jašek, O. (CZ)
Zajíčková, L. (CZ)
Vondráček, Martin (FZU-D) RID, ORCID
Zbořil, R. (CZ)
Mašláň, M. (CZ)Celkový počet autorů 7 Zdroj.dok. Mössbauer Spectroscopy in Materials Science - 2010. - Melville, New York : American Institute of Physics, 2010 / Tuček J. ; Miglierini M. - ISSN 0094-243X - ISBN 978-0-7354-0806-7 Rozsah stran s. 90-95 Poč.str. 6 s. Akce MSMS 10 - Mossbauer Spectroscopy in Materials Science 2010 Datum konání 31.01.2010-05.02.2010 Místo konání Liptovský Ján Země SK - Slovensko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova nanotubes ; Mossbauer ; iron ; carbides Vědní obor RIV BM - Fyzika pevných látek a magnetismus CEP 1M0512 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy CEZ AV0Z20410507 - UFM-A (2005-2011) AV0Z10100521 - FZU-D (2005-2011) UT WOS 000281606200012 DOI 10.1063/1.3473904 Anotace Phase composition of ~10 nm thick Fe film on the silicon substrate with 200 nm thick SiOx layer after annealing in vacuum and in H2+CH4 was investigated using Conversion Electron Mössbauer spectroscopy (CEMS) . CEMS spectra show that the original iron film was formed by Fe3+ phase. This phase is stable after the annealing in vacuum or in CH4+H2 below 500 °C but formation of phases with Fe2+ and Fe0 (γ-Fe and α-Fe) was observed after annealing at 500 °C and higher temperatures. Formation of fayalite (Fe2SiO4) occurred during vacuum annealing at 700 °C. SEM and CEMS study of the sample with grown multi-walled carbon nanotubes shows that the dominating part of iron atoms is present in Fe3C and Fe5C2 carbide phases. Besides their stoichiometric forms spectrum components which can be ascribed to the amorphous Fe5-xC2+x carbides, γ-Fe, and Fe3+ were observed there. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2011
Počet záznamů: 1