Powders with superparamagnetic Fe3C particles studied with Mössbauer spectrometry

  1. 1.
    SYSNO ASEP0354265
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevPowders with superparamagnetic Fe3C particles studied with Mössbauer spectrometry
    Tvůrce(i) David, Bohumil (UFM-A) RID
    Schneeweiss, Oldřich (UFM-A) RID, ORCID
    Dumitrache, F. (RO)
    Fleaca, C. (RO)
    Alexandrescu, R. (RO)
    Morjan, I. (RO)
    Zdroj.dok.Journal of Physics: Conference Series. - : Institute of Physics Publishing - ISSN 1742-6588
    Roč. 217, č. 1 (2010), 012097
    Poč.str.4 s.
    AkceInternational Conference on the Applications of the Mossbauer Effect (ICAME 2010)
    Datum konání19.07.2009-24.07.2009
    Místo konáníVídeň
    ZeměAT - Rakousko
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.GB - Velká Británie
    Klíč. slovaFe3C ; superparamagnetism ; Mössbauer spectroscopy ; magnetic measurements ; laser-induced pyrolysis
    Vědní obor RIVBM - Fyzika pevných látek a magnetismus
    CEPGA202/08/0178 GA ČR - Grantová agentura ČR
    1M0512 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
    CEZAV0Z20410507 - UFM-A (2005-2011)
    UT WOS000287181700097
    DOI10.1088/1742-6596/217/1/012097
    AnotaceTwo nanopowders with superparamagnetic Fe3C particles were synthesised by the method of laser-induced pyrolysis of gaseous precursors. Both were characterised by X-ray diffraction, Mössbauer spectrometry and standard magnetic measurements. The mean crystallite size of Fe3C was 3 nm for the first sample and 10 nm for the second sample (Scherrer formula), i.e. it was lower than in our previously studied ferromagnetic Fe 3C-based sample. Fe3C phase in both present samples exhibited by 20 K reduced Curie temperature which is interpreted as a nanosize effect. After annealing of the samples at 1073 K for 30 minutes the Curie temperature of the Fe3C phase in both samples matched its standard bulk value. Beside Fe3C phase also Fe3O4 and carbon black were present in the synthesised samples.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2011
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.