Effect of heat treatments with a pointed cooling on the mechanical compression properties of TiAl intermetalic
- 1.
SYSNO ASEP 0354170 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Effect of heat treatments with a pointed cooling on the mechanical compression properties of TiAl intermetalic Tvůrce(i) Petrenec, Martin (UFM-A)
Kruml, Tomáš (UFM-A) RID, ORCID
Zemanová, Adéla (UFM-A) RID, ORCID
Krahula, Karel (UFM-A)Zdroj.dok. Metal 2010. 19th International conference on metallurgy and materials - Conference Proceedings. - Ostrava : Tanger s.r.o., 2010 - ISBN 978-80-87294-17-8 Rozsah stran s. 828-833 Poč.str. 6 s. Akce Metal 2010. International Conference on Metallurgy and Materials /19./ Datum konání 18.05.2010-20.05.2010 Místo konání Rožnov pod Radhoštěm Země CZ - Česká republika Typ akce EUR Jazyk dok. eng - angličtina Země vyd. CZ - Česká republika Klíč. slova graded cooling heat treatments ; DTA curve ; TiAl-8Nb intermetallics ; fully lamellar microstructure ; compression tests Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP GA106/08/1631 GA ČR - Grantová agentura ČR CEZ AV0Z20410507 - UFM-A (2005-2011) UT WOS 000286658700143 Anotace The influence of the graded cooling heat treatments on a change in the structure and the room temperature mechanical compression properties of cast Ti-44Al-8Nb intermetallic were studied. The coolings were the air cooling and the graded cooling which was composed of combination of furnace cooling and air cooling for selected two temperatures 1315 °C and 1200 °C. These selected temperatures were used from the measuring of the differential thermal analysis (DTA). All heat treatments used remold the cast nearly lamellar structure ?/?2 to the fully lamellar uniform structure and decreased the average grain size to the half. The air cooling and the graded cooling with temperature 1315 °C were produced in higher yield stress and lower plasticity due the very thin lamellar thickness and planar grain boundary. While higher plasticity and lower yield stress are obtained using the graded cooling with temperature 1200 °C. It is caused by the very thick lamellar spacing and locked grain boundaries. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2011
Počet záznamů: 1