Fatigue properties of Fe-Al intermetallic coatings prepared by plasma spraying

  1. 1.
    SYSNO ASEP0353721
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevFatigue properties of Fe-Al intermetallic coatings prepared by plasma spraying
    Tvůrce(i) Mušálek, Radek (UFP-V) RID, ORCID
    Kovářík, O. (CZ)
    Skiba, Tomáš (UFP-V)
    Haušild, P. (CZ)
    Karlík, M. (CZ)
    Colmenares-Angulo, J. (US)
    Zdroj.dok.Intermetallics. - : Elsevier - ISSN 0966-9795
    Roč. 18, č. 7 (2010), s. 1415-1418
    Poč.str.5 s.
    Forma vydáníweb - web
    AkceFEAL 2009 - 5th Discussion Meeting on the Development of Innovative Iron Aluminium Alloys
    Datum konání21.09.2009-24.09.2009
    Místo konáníPrague
    ZeměCZ - Česká republika
    Typ akceWRD
    Jazyk dok.eng - angličtina
    Země vyd.GB - Velká Británie
    Klíč. slovaIron aluminides ; Fatigue resistance and crack growth ; plasma spraying ; scanning electron microscopy
    Vědní obor RIVJK - Koroze a povrchové úpravy materiálů
    CEPME 901 GA MŠMT - Ministerstvo školství, mládeže a tělovýchovy
    CEZAV0Z20430508 - UFP-V (2005-2011)
    UT WOS000279568600032
    DOI10.1016/j.intermet.2010.02.001
    AnotaceIn this research, FeAl based coatings were deposited on low carbon steel using two different plasma spraying technologies – gas stabilized plasma gun (GSP) and water stabilized plasma gun (WSP) – resulting in different deposition conditions. Significant changes in local chemical composition compared to feedstock material were observed due to uneven evaporation of Fe and Al from the molten material during the interaction of feedstock with plasma. Influence of coatings on substrate fatigue properties was characterized at room temperature using special testing device ‘‘SF-Test’’. Fatigue lifetimes of specimens with different coatings were compared with those of uncoated specimens. Fractographic analysis of failed specimens revealed that substrate fatigue cracks initiated at coating–substrate interface and grew by striation mechanism. The coatings failed due to intrasplat cracking and intersplat decohesion.
    PracovištěÚstav fyziky plazmatu
    KontaktVladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975
    Rok sběru2011
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.