Odified polysiloxane based ceramic matrix for long fibre reinforced composite materials

SYSNO ASEP	0353409
Druh ASEP	C - Konferenční příspěvek (mezinárodní konf.)
Zařazení RIV	D - Článek ve sborníku
Název	Odified polysiloxane based ceramic matrix for long fibre reinforced composite materials
Tvůrce(i)	Chlup, Zdeněk (UFM-A)_{RID, ORCID} Černý, Martin (USMH-B)_{RID, ORCID, SAI} Strachota, Adam (UMCH-V)_{RID, ORCID} Kozák, Vladislav (UFM-A)_{RID, ORCID}
Celkový počet autorů	4
Zdroj.dok.	ECCM14 - European Conference on Composite Materials. - Budapešť : Budapest University of Technology and Economics, Department of Polymer Engineering, 2010 / László KOLLÁR ; Tibor CZIGÁNY ; József KARGER-KOCSIS - ISBN 978-963-313-008-7
Rozsah stran	s. 1-10
Poč.str.	10 s.
Forma vydání	USB flash disk - USB flash disk
Akce	European Conference on Composite Materials (ECCM14)
Datum konání	07.06.2010-10.06.2010
Místo konání	Budapešť
Země	HU - Maďarsko
Typ akce	WRD
Jazyk dok.	eng - angličtina
Země vyd.	HU - Maďarsko
Klíč. slova	polysiloxane ; pyrolysis ; indentation
Vědní obor RIV	JH - Keramika, žáruvzdorné materiály a skla
CEP	GA106/09/1101 GA ČR - Grantová agentura ČR
CEZ	AV0Z20410507 - UFM-A (2005-2011)
	AV0Z40500505 - UMCH-V (2005-2011)
	AV0Z30460519 - USMH-B (2005-2011)
Anotace	The main goal of the work was preparation of cost effective and simple to pre-shape high temperature composite material. To fulfil expectations it was necessary to optimise the design of the composite to have an optimal fibre-matrix interaction. Fracture behaviour of matrix prepared by pyrolysis of various modification of polysiloxane resin used for preparation of composites reinforced by long ceramics fibres was under investigation and findings were summarised in this contribution. A number of modified polysiloxane resin was studied in various steps of heat treatment as a stay alone materials to enable optimisation of matrix properties. Fully instrumented indentation technique for determination of reliable parameters characterising microstructural changes was used. Both optical and scanning electron microscopy was employed in microstructural observations and fracture mechanism qualification.