Different creep behaviour and microstructure of ECAP aluminium with the identical ECAP history

  1. 1.
    SYSNO ASEP0349529
    Druh ASEPC - Konferenční příspěvek (mezinárodní konf.)
    Zařazení RIVD - Článek ve sborníku
    NázevDifferent creep behaviour and microstructure of ECAP aluminium with the identical ECAP history
    Tvůrce(i) Král, Petr (UFM-A) RID, ORCID
    Dvořák, Jiří (UFM-A) RID, ORCID
    Sklenička, Václav (UFM-A) RID, ORCID
    Svoboda, Milan (UFM-A) RID, ORCID
    Celkový počet autorů4
    Zdroj.dok.METAL 2010. Conference proceedings. - Ostrava : Tanger, s.r.o, 2010 - ISBN 978-80-87294-15-4
    Rozsah strančl. pe10
    Poč.str.6 s.
    Forma vydáníCD-ROM - CD-ROM
    AkceMetal 2010. International Conference on Metallurgy and Materials /19./
    Datum konání18.05.2010-20.05.2010
    Místo konáníRožnov pod Radhoštěm
    ZeměCZ - Česká republika
    Typ akceEUR
    Jazyk dok.eng - angličtina
    Země vyd.CZ - Česká republika
    Klíč. slovaorientation image microscopy ; creep ; ultrafine - grained microstructure
    Vědní obor RIVJJ - Ostatní materiály
    CEPGPP108/10/P469 GA ČR - Grantová agentura ČR
    CEZAV0Z20410507 - UFM-A (2005-2011)
    AnotaceExperiments were conducted on extremely coarse - grained Al (99.99%. The subsequent extrusion passes were performed by route A (no rotation between subsequent passes) up to 2 ECAP passes. Creep tests in tension were performed on the as-pressed samples at 473 K and applied stress 15 MPa. It was found that the ultrafine - grained Al specimens with the same ECAP history showed the scatter in the creep properties. In this work the microstructure changes within grains with different crystallographic orientations and near their high - angle boundaries of coarse-grained state in the sample after different ECAP passes were studied. Mutual comparison of the results of microstructural characterization of microstructure of as-received coarse-grained state and the state after different ECAP passes were performed. It is concluded that the scatter in creep properties could be influenced by inhomogeneity of ECAP microstructure.
    PracovištěÚstav fyziky materiálu
    KontaktYvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485
    Rok sběru2011
Počet záznamů: 1  

  Tyto stránky využívají soubory cookies, které usnadňují jejich prohlížení. Další informace o tom jak používáme cookies.