Effect of different number of ECAP passes on creep in Cu-Zr alloy

SYSNO ASEP	0349522
Druh ASEP	C - Konferenční příspěvek (mezinárodní konf.)
Zařazení RIV	D - Článek ve sborníku
Název	Effect of different number of ECAP passes on creep in Cu-Zr alloy
Tvůrce(i)	Král, Petr (UFM-A)_{RID, ORCID} Dvořák, Jiří (UFM-A)_{RID, ORCID} Svoboda, Milan (UFM-A)_{RID, ORCID} Kvapilová, Marie (UFM-A)_{RID, ORCID} Sklenička, Václav (UFM-A)_{RID, ORCID}
Celkový počet autorů	5
Zdroj.dok.	Metal 2010. 19th International conference on metallurgy and materials - Conference Proceedings. - Ostrava : Tanger s.r.o., 2010 - ISBN 978-80-87294-17-8
Rozsah stran	s. 736-740
Poč.str.	5 s.
Akce	Metal 2010. International Conference on Metallurgy and Materials /19./
Datum konání	18.05.2010-20.05.2010
Místo konání	Rožnov pod Radhoštěm
Země	CZ - Česká republika
Typ akce	EUR
Jazyk dok.	eng - angličtina
Země vyd.	CZ - Česká republika
Klíč. slova	ultrafine-grained microstructure ; creep ; equal-channel angular pressing
Vědní obor RIV	JJ - Ostatní materiály
CEP	GPP108/10/P469 GA ČR - Grantová agentura ČR
CEZ	AV0Z20410507 - UFM-A (2005-2011)
UT WOS	000286658700125
Anotace	A coarse-grained binary Cu-0.2wt%Zr alloy was processed by equal-channel angular pressing (ECAP) in order to evaluate the effect of severe plastic deformation on the thermal stability of resulting ultrafine-grained microstructure after ECAP and on creep behaviour of the pressed alloy. Constant stress creep tests in tension were conducted at temperature 673 K and at the different applied stresses. It was found that the Cu-0.2Zr alloy after the first four ECAP passes exhibited higher creep resistance by comparison with unpressed state. However, the alloy processed by 8 ECAP passes showed faster creep rate than unpressed material under the same loading conditions. The measured value of stress exponent of the creep rate n~6 indicates possibility of an intragranular deformation mechanism as the rate-controlling process in creep of an alloy after 8 ECAP passes. Furthermore, creep behaviour of ECAPed material may be influenced by mesoscopic boundary sliding along shear bands.
Pracoviště	Ústav fyziky materiálu
Kontakt	Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485