Plasma Spraying of Refractory Cermets by the Water-Stabilized Spray (WSP) System
- 1.
SYSNO ASEP 0336035 Druh ASEP C - Konferenční příspěvek (mezinárodní konf.) Zařazení RIV D - Článek ve sborníku Název Plasma Spraying of Refractory Cermets by the Water-Stabilized Spray (WSP) System Překlad názvu Plazmové nástřiky vysokotavitelných kovokeramik pomocí plazmatronu s vodní stabilizací Tvůrce(i) Ctibor, Pavel (UFP-V) RID, ORCID
Brožek, Vlastimil (UFP-V) RID
Chráska, Pavel (UFP-V) RID
Cheong, D.-I. (KR)
Yang, S.-H. (KR)Zdroj.dok. ITSC 2009 Proceedings from the 2009 International Thermal Spray Conference. - Las Vegas : ITSC Partner Societies, 2009 / Marple B.R. ; Hyland M.M. ; Lau Y.-C. ; Li C.-J. ; Lima R.S. ; Montavon G. - ISBN 978-1-61503-004-0 Rozsah stran s. 824-829 Poč.str. 6 s. Forma vydání CD ROM 05271A - CD ROM 05271A Akce Thermal Spray 2009: International Thermal Spray Conference Datum konání 04.05.2009-07.05.2009 Místo konání Las Vegas Země US - Spojené státy americké Typ akce WRD Jazyk dok. eng - angličtina Země vyd. US - Spojené státy americké Klíč. slova Plasma spraying ; refractory cermets ; tungsten cermets ; zirconium carbide Vědní obor RIV JH - Keramika, žáruvzdorné materiály a skla CEZ AV0Z20430508 - UFP-V (2005-2011) Anotace Among important metal matrix composites are cemented carbides, predominantly tungsten carbide with cobalt binder. For high temperature applications, e.g., in nuclear or thermonuclear reactors technology, metals with a higher melting point, namely, tungsten, are preferred. Tungsten carbides with a decomposition temperature of 2785°C should also be replaced by, for example, ZrC. Bulk parts can be produced by powder metallurgy techniques but plasma spraying of cermets could be an interesting alternative. A mixture of W powder was prepared with 3 to 20 vol. % of ZrC. This feedstock having a spheroidal character was fed into the plasma of the water-stabilized plasma (WSP®) gun by means of an inert gas carrier. Coatings of a thickness of about 1 mm were sprayed on various substrates, namely, graphite. Pure tungsten and pure ZrC were sprayed under similar conditions. Microhardness, surface roughness, XRD, XRF, dilatometry and spectroscopic techniques (Raman microspectroscopy) were used Pracoviště Ústav fyziky plazmatu Kontakt Vladimíra Kebza, kebza@ipp.cas.cz, Tel.: 266 052 975 Rok sběru 2010
Počet záznamů: 1