Formation of Layered Double Hydroxides on Alumina Surface in Aqueous Solutions Containing Divalent Metal Cations

SYSNO ASEP	0333297
Druh ASEP	J - Článek v odborném periodiku
Zařazení RIV	J - Článek v odborném periodiku
Poddruh J	Článek ve WOS
Název	Formation of Layered Double Hydroxides on Alumina Surface in Aqueous Solutions Containing Divalent Metal Cations
Překlad názvu	Tvorba LDH na povrchu aluminy v roztocích obsahujících divalentní kovové ionty
Tvůrce(i)	Kovanda, F. (CZ) Mašátová, P. (CZ) Novotná, P. (CZ) Jirátová, Květa (UCHP-M)_{RID, ORCID, SAI}
Zdroj.dok.	Clays and Clay Minerals. - : Springer - ISSN 0009-8604 Roč. 57, č. 4 (2009), s. 425-432
Poč.str.	8 s.
Jazyk dok.	eng - angličtina
Země vyd.	US - Spojené státy americké
Klíč. slova	deposition ; layered double hydroxides ; supported mixed oxides
Vědní obor RIV	CI - Průmyslová chemie a chemické inženýrství
CEP	GA104/07/1400 GA ČR - Grantová agentura ČR
CEZ	AV0Z40720504 - UCHP-M (2005-2011)
UT WOS	000271401600003
DOI	10.1346/CCMN.2009.0570403
Anotace	A formation of layered double hydroxides (LDHs) on an Al2O3/Al support prepared by anodic oxidation of aluminum foil was studied in diluted aqueous solutions of Co, Mn, and/or Ni nitrates. The LDH deposition was carried out under hydrothermal conditions at 80 – 180 °C for time ranging from 8 to 168 hours. The LDH phase was formed after long-term deposition (3 – 7 days) at 120 – 160 °C and only a slight incorporation of Mn into the deposited LDHs was found. Ni cations when present in the solution were preferentially incorporated into the LDH phase; a homogeneous layer was formed, with single platy crystals oriented perpendicularly towards the support. After calcination at 500 °C, the products formed on Al2O3/Al support exhibited worse reducibility in comparison with mixed oxides obtained by thermal decomposition of coprecipitated LDHs.