Through-the-thickness residual stress analysis by neutron diffraction in inoxidizable martensitic steel samples with and without tungsten carbide coating

  1. 1.
    SYSNO ASEP0332832
    Druh ASEPJ - Článek v odborném periodiku
    Zařazení RIVJ - Článek v odborném periodiku
    Poddruh JČlánek ve WOS
    NázevThrough-the-thickness residual stress analysis by neutron diffraction in inoxidizable martensitic steel samples with and without tungsten carbide coating
    Překlad názvuAnalýza zbytkového napětí přes tloušťku neutronovou difrakcí ve vzorcích nerezové martenzitické oceli s povlakem z karbidu wolframu a bez něj
    Tvůrce(i) Rogante, M. (IT)
    Mikula, Pavol (UJF-V) RID, ORCID, SAI
    Vrána, Miroslav (UJF-V) RID
    Zdroj.dok.Surface and Coatings Technology. - : Elsevier - ISSN 0257-8972
    Roč. 204, č. 5 (2009), s. 650-656
    Poč.str.7 s.
    Jazyk dok.eng - angličtina
    Země vyd.CH - Švýcarsko
    Klíč. slova13Cr4Ni steel ; residual stress ; Coating
    Vědní obor RIVBG - Jaderná, atomová a mol. fyzika, urychlovače
    CEZAV0Z10480505 - UJF-V (2005-2011)
    UT WOS000271433800015
    DOI10.1016/j.surfcoat.2009.08.044
    AnotaceThe residual stress (RS) induced in the substrateby thermal spray-coating was studied. Two 3Cr4Ni inoxidizable martensitic steel samples, one having a thermal spray (WC–12%Co) HVOF coated surface, the other a shoot peened surface,were analyzed byneutron diffraction (ND) in order to determine the real RS depth-profile and investigate the effects of the thermal process on the considered materials. The stresses resulted in the range from −80 to 50 MPa for the uncoated sample, while for the coated sample they increased gradually from a slight compressive status in correspondence of the uncoated surface, to greatest values of ~250 MPa in correspondence of the coating. A traditional X-ray investigation on the coated surface measured compressive RS values σ=−550±40 MPa, showing that ND investigation is very suitable for critical applications, where a much greater stress situation could be prezent at a diverse depth.
    PracovištěÚstav jaderné fyziky
    KontaktMarkéta Sommerová, sommerova@ujf.cas.cz, Tel.: 266 173 228
    Rok sběru2010