Silica encapsulated manganese perovskite nanoparticles for magnetically induced hyperthermia without the risk of overheating
- 1.
SYSNO ASEP 0332064 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Článek ve WOS Název Silica encapsulated manganese perovskite nanoparticles for magnetically induced hyperthermia without the risk of overheating Překlad názvu Nanočástice manganatého perovskitu obalené oxidem křemičitým pro magneticky indukovanou hypertermii bez rizika přehřátí Tvůrce(i) Kaman, Ondřej (FZU-D) RID, ORCID
Pollert, Emil (FZU-D)
Veverka, Pavel (FZU-D) RID, ORCID
Veverka, Miroslav (FZU-D) RID
Hadová, Eva (FZU-D)
Knížek, Karel (FZU-D) RID, ORCID
Maryško, Miroslav (FZU-D) RID
Kašpar, P. (CZ)
Klementová, Mariana (UACH-T) RID, SAI, ORCID
Grünwaldová, V. (CZ)
Vasseur, S. (FR)
Epherre, R. (FR)
Mornet, S. (FR)
Goglio, G. (FR)
Duguet, E. (FR)Zdroj.dok. Nanotechnology. - : Institute of Physics Publishing - ISSN 0957-4484
Roč. 20, č. 27 (2009), 275610/1-275610/7Poč.str. 7 s. Jazyk dok. eng - angličtina Země vyd. GB - Velká Británie Klíč. slova manganese perovskite ; hyperthermia ; nanoparticles Vědní obor RIV BM - Fyzika pevných látek a magnetismus CEP KAN200200651 GA AV ČR - Akademie věd KJB100100701 GA AV ČR - Akademie věd CEZ AV0Z10100521 - FZU-D (2005-2011) AV0Z40320502 - UACH-T (2005-2011) UT WOS 000267089600022 DOI 10.1088/0957-4484/20/27/275610 Anotace Nanoparticles of manganese perovskite of the composition La0.75Sr0.25MnO3 uniformly coated with silica were prepared by encapsulation of the magnetic cores (mean crystallite size 24 nm) using tetraethoxysilane followed by fractionation. The resulting hybrid particles form a stable suspension in an aqueous environment at physiological pH and possess a narrow hydrodynamic size distribution. Both calorimetric heating experiments and direct measurements of hysteresis loops in the alternating field revealed high specific power losses, further enhanced by the encapsulation procedure in the case of the coated particles. The corresponding results are discussed on the basis of complex characterization of the particles and especially detailed magnetic measurements. Moreover, the Curie temperature (335 K) of the selected magnetic cores resolves the risk of local overheating during hyperthermia treatment. Pracoviště Fyzikální ústav Kontakt Kristina Potocká, potocka@fzu.cz, Tel.: 220 318 579 Rok sběru 2010