Low cycle fatigue of austempered ductile cast iron alloyed with nickel at room and at depressed temperature
- 1.
SYSNO ASEP 0331756 Druh ASEP J - Článek v odborném periodiku Zařazení RIV J - Článek v odborném periodiku Poddruh J Ostatní články Název Low cycle fatigue of austempered ductile cast iron alloyed with nickel at room and at depressed temperature Tvůrce(i) Petrenec, Martin (UFM-A)
Beran, Přemysl (UJF-V) RID, ORCID, SAI
Šmíd, Miroslav (UFM-A) RID, ORCID
Roupcová, Pavla (UFM-A) RID, ORCID
Tesařová, H. (CZ)Celkový počet autorů 5 Zdroj.dok. Materiálové inžinierstvo - Materials Engineering - ISSN 1335-0803
Roč. 16, 3a (2009), s. 1-6Poč.str. 6 s. Akce Degradácia konštrukčných materiálov 2009 Datum konání 02.09.2009-04.09.2009 Místo konání Tatranská Lomnica Země SK - Slovensko Typ akce WRD Jazyk dok. eng - angličtina Země vyd. SK - Slovensko Klíč. slova Low cycle fatigue ; ADI with nickel alloying ; Neutron diffraction ; Fatigue crack initiation ; Depressed temperature Vědní obor RIV JL - Únava materiálu a lomová mechanika CEP 1QS200410502 GA AV ČR - Akademie věd CEZ AV0Z20410507 - UFM-A (2005-2011) AV0Z10480505 - UJF-V (2005-2011) Anotace Total strain controlled tests have been performed on cylindrical specimens of austempered ductile cast iron (ADI) with the aim to compare cyclic plasticity and the fatigue life at temperatures 23°C and –45°C. The measurement of retained austenite by neutron diffraction before and after fatigue tests is used to discuss the cyclic stress-strain response. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained for both temperatures. Cyclic stress-strain curve obtained at -45°C is shifted to higher stress amplitudes relative to room temperature curve. The fatigue life curves at both temperatures can be well approximated by the Manson-Coffin and Basquin laws.The Manson-Coffin curves are identical at both temperatures while the Basquin curve is shifted to longer fatigue life. Fatigue cracks initiated preferably from persistent slip markings at the interface of graphite nodule and the ausferrite matrix. Pracoviště Ústav fyziky materiálu Kontakt Yvonna Šrámková, sramkova@ipm.cz, Tel.: 532 290 485 Rok sběru 2010
Počet záznamů: 1